The paper presents the results of a laboratory investigation of the microbiologically assisted hydrogen‐induced stress cracking (HISC) of 2,205 duplex stainless steel (DSS). The testing of susceptibility toward HISC was performed with two different methods. Precharged in sulfate‐reducing bacteria (SRB), inoculated medium samples were subjected to slow strain‐rate testing in artificial seawater. In situ constant load tests were performed directly in SRB‐inoculated medium under hydrogen charging at 70% of the ultimate tensile strength. Samples tested in the biotic (SRB) conditions showed a considerable loss of ductility as compared to those tested in sterile conditions. Quantitative characteristics of fracture surfaces indicated increased susceptibility to HISC of biotic samples, therefore, suggesting a role of SRB in promoting hydrogen damage of DSS.
Cytowania
-
5
CrossRef
-
0
Web of Science
-
5
Scopus
Autorzy (4)
-
Tomasz Rzychoń dr inż.
- Politechnika Śląska, Wydział Mechaniczny Technologiczny
-
Wojciech Simka dr inż.
- Politechnika Śląska, Wydział Chemiczny
-
Joanna Michalska dr inż.
- Politechnika Śląska, Wydział Chemiczny
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
nr 70,
strony 1667 - 1681,
ISSN: 0947-5117 - Język:
- angielski
- Rok wydania:
- 2019
- Opis bibliograficzny:
- Łabanowski J., Rzychoń T., Simka W., Michalska J.: Sulfate‐reducing bacteria‐assisted hydrogen‐induced stress cracking of 2205 duplex stainless steels// MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION. -Vol. 70, iss. 9 (2019), s.1667-1681
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1002/maco.201910802
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 115 razy