Weldability of pipe grade polyethylenes as realized from thermal and mechanical properties assessments
Abstrakt
Since polyethylene (PE) has been widely accepted for the production of high-pressure fluid conveying pipelines, studies devoted to weldability of PE connections were always of major importance. In this study, two industrial PE grades designed for pipe production, namely PE80 and PE100, were injection molded, cut, and then welded as PE100-PE100, PE100-PE80, and PE80-PE80. The heat-welded joints were assessed by differential scanning calorimetry and tensile measurements. The results obtained from thermal and mechanical analyses were compared with equivalents for aged samples. Thermal analysis revealed that the melting point of the PE100-PE100 sample is obviously larger than the one for the PE80-PE80 joint, for the PE80 chains deteriorate the crystallization of PE100. Further, the PE80-PE80 sample showed the lowest lamellar thickness and crystalline molecular weight among the studied joints. The aging process was found to increase lamellar thickness and molecular weight, though in the PE100-PE100 sample such quantities very limitedly increased. The yield stress of aged joints was higher than that for just-prepared samples, while an inverse trend was seen for strain at break. From a practical viewpoint, the PE100-PE100 welds offer better properties.
Cytowania
-
3
CrossRef
-
0
Web of Science
-
3
Scopus
Autorzy (6)
-
Vahabodin Goodarzi
- Baqiyatallah University of Medical Sciences, Tehran, Iran Applied Biotechnology Research Center
-
Zahed Ahmadi
- Amirkabir University of Technology, Tehran, Iran Color and Polymer Research Center
-
Mohammad Saeb
- Institute for Color Science and Technology, ehran, Iran Department of Resins and Additives
-
Farkhondeh Hemmati
- Amirkabir University of Technology, Tehran, Iran Department of Polymer Engineering and Color Technology
-
Mehdi Ghaffari
- Golestan University, Gorgan, Golestan, Iran Polymer Group
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF POLYMER ENGINEERING
nr 36,
wydanie 8,
strony 853 - 860,
ISSN: 0334-6447 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Goodarzi V., Ahmadi Z., Saeb M., Hemmati F., Ghaffari M., Formela K.: Weldability of pipe grade polyethylenes as realized from thermal and mechanical properties assessments// JOURNAL OF POLYMER ENGINEERING. -Vol. 36, iss. 8 (2016), s.853-860
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1515/polyeng-2015-0242
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 136 razy
Publikacje, które mogą cię zainteresować
Underwater wet welding of S1300 ultra-high strength steel
- J. Tomków,
- M. Landowski,
- D. Fydrych
- + 1 autorów
Giant Reed (Arundo donax L.) Fiber Extraction and Characterization for Its Use in Polymer Composites
- L. Suárez,
- M. Barczewski,
- P. Kosmela
- + 1 autorów
Mechanical, Thermal and Rheological Properties of Polyethylene-Based Composites Filled with Micrometric Aluminum Powder
- O. Mysiukiewicz,
- P. Kosmela,
- M. Barczewski
- + 1 autorów
Role of buttering layer composition on microstructural heterogeneity and mechanical properties of Alloy 617 and P92 steel dissimilar welded joints for future Indian AUSC program
- S. Rathore,
- A. Kumar,
- S. Sirohi
- + 4 autorów