Zr‐Based Metal‐Organic Framework UiO‐66/Ultem® 1000 Membranes for Effective CO2/H2 Separation

Abstrakt

Mixed-matrix membranes (MMMs) using UiO-66 nanofillers as dispersing inorganic phase and polyetherimide (PEI) as continuous polymeric matrix were synthesized. Different UiO-66 loadings of 10, 20, and 30 wt % were applied. The morphology and UiO-66 dispersion over the prepared MMMs were examined. Gas separation measurements were performed for H2/CO2 gas mixture to evaluate the influence of UiO-66 on the separation yield of resulting membranes. When compared with pristine PEI membranes, MMMs containing metal-organic framework (MOF) nanoparticles revealed superior H2 permeability and H2/CO2 separation factor, e.g., maximum permeability values of 14.6 and 5.5 Barrer were observed for H2 and CO2 at a filler loading of 10 wt % and an applied pressure of 4.0 bar.

Cytowania

  • 4

    CrossRef

  • 0

    Web of Science

  • 4

    Scopus

Autorzy (6)

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach
Opublikowano w:
CHEMICAL ENGINEERING & TECHNOLOGY nr 46, strony 2046 - 2053,
ISSN: 0930-7516
Język:
angielski
Rok wydania:
2023
Opis bibliograficzny:
Imad M., Castro Munoz R., Bernauer M., Martin V., Izak P., Fíla V.: Zr‐Based Metal‐Organic Framework UiO‐66/Ultem® 1000 Membranes for Effective CO2/H2 Separation// CHEMICAL ENGINEERING & TECHNOLOGY -Vol. 46,iss. 10 (2023), s.2046-2053
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1002/ceat.202200599
Źródła finansowania:
  • Publikacja bezkosztowa
Weryfikacja:
Politechnika Gdańska

wyświetlono 75 razy

Publikacje, które mogą cię zainteresować

Meta Tagi