This paper concerns an inspection of a water supply system, made of AISI 304 steel, which showed signs of local corrosion at the weld. Such corrosion caused material perforation after very short periods of operation. It was revealed that steel was sensitised during the welding process. It was also proven that chromium micro-segregation occurred in the alloy leading to galvanic cell formation which initialised the process of pitting...

Case study of corrosion failure of urban water supply system caused by the harmful effects of stray currents was presented. The failure occurred at a site distant from the sources of these currents namely the tramway and railway traction systems. Diagnosis revealed the stray currents flow to pipeline over a remote distance of 800 ÷ 1,000 meters from the point of failure. At the point of failure stray currents flowed from the pipeline...

In this research effect of the addition of multi-wall carbon nanotubes (MWCNTs) as additive powder on microstructure and corrosion behavior of fabricated Al-CNT composites was studied. The aluminum powder and CNTs were mixed with high energy planetary ball-mill. It is observed that by increasing milling time, the uniformity of CNTs on aluminum matrix and consequently corrosion resistance of Al-CNT composite is increased. On the...

This study investigates the corrosion behavior of dissimilar gas tungsten arc (GTA) welded joints between super duplex stainless steel (sDSS 2507) and pipeline steel (X-70) using electrochemical and immersion corrosion tests. The GTA welds were fabricated using ER2594 and ER309L fller metals. The study examined the electrochemical characteristics and continuous corrosion behavior of samples extracted from various zones of the weldments...

In the recent years atomic force microscopy is recognized as valuable tool for investigation of surficial features of construction materials. It concerns, among other things, studies of changes caused by such phenomena as galvanic corrosion, passivation associated with the growth of oxide layers, or sensitization of austenitic steels with the formation of carbide phases. In addition, atomic forcemicroscopy allows easy coupling...