The article presents the influence of heat treatment on the kinetics of transformations in lean duplex LDX2101 steel and a weld made of standard duplex 2209 material, which was welded by manual metal arc welding. Changes in the microstructure, hardness, and magnetic phase content were analyzed after heat treatment was conducted at a temperature of 800 °C for a period ranging from 15 to 1440 min. Light and scanning microscopy, Vickers...

The weldability of steel under the water is limited due to the influence of the environment. Water causes limited visibility, presence of the residual stresses, increasing the cooling rate, and increasing the diffusible hydrogen content in deposited metal, leading to the formation of brittle microstructures in heat-affected zone (HAZ). The paper presents the results of mechanical properties testing of S420G2+M steel welded joints...

The determination of diffusible hydrogen content in deposited metal of P 62 MR covered electrodes for manual metal arc welding by mercury method was carried out. The test results indicate that covered electrodes 62 P MR grade generate a mean of 4.02 ml/100g of diffusible hydrogen in deposited metal, which is consistent with H5 class.

ABSTRACT The present work was conducted to assess the weldability of duplex stainless steel in underwater conditions. Metal manual arc welding (MMA) with the use of coated electrodes was used in the investigations. Tekken weldability tests were performed underwater at 0.5 m depth and in the air. Nondestructive tests, metallographic examinations of welds, ferrite content assessment in microstructure and hardness test were performed....