Niobium-doped strontium titanate synthesized via conventional solid-state reaction has been studied. Influence of niobium content on the lattice parameters and electrical conductivity has been reported. Various reduction conditions have been investigated. For samples reduced in hydrogen at 1400°C, a transition from thermally activated to metallic behavior has been observed. Maximum electrical conductivity (ca. 55 Scm−1 at 650°C)...

Przebadano wpływ zawartości niobu na strukturę i własności elektryczne tytanianu strontu. Zbadany został wpływ warunków redukcji i porowatości na właściwości materiału. Za optymalne uznano domieszkowanie niobem w wysokości 2% molowych.

Yttria and iron co-doped strontium titanate perovskites, (Y0,07Sr0,93Ti1-xFexO3-δx=0,1; 0,2) samples were fabricated by two methods: solid-state synthesis (SS) and the Pechinisol-gel modified method. The morphology of samples were measured by SEM and X-raydiffraction. Results were compared and discussed. The strong relationship between fabricationprocedure and microstructure has been proven. It was also observed, that the nanoceramicsobtained...

In this paper, a novel electrode material based on Pr, Ni co-doped strontium titanate ( Sr0.7Pr0.3)xTi1−yNiyO3 with constant amount of 30% praseodymium dopant, different amount of nickel (y = 0.06 and y = 0.10) and additional nonstoichiometry in Sr-site (x = 1; x = 0.9 and x = 0.8) was investigated as fuel electrode for SOEC devices. A porous ceramics were prepared by solid-state reaction method. X-ray diffraction measurements...

The yttrium, iron and niobium doped-SrTiO3 powders have been successfully fabricated by a modified low–temperature synthesis method from a polymer complex. The usage of strontium hydroxide precursor instead of conventional strontium nitrate or strontium carbonate provides to the possibility of significant decrease of annealing temperature. It allows to prepare a material with sphere-shape grains of nanometric size (15–70 nm). The...