The ferromagnetic superconductor Y9Co7 was chemically doped to yield the solid solution Y9Co7-xPdx for 0 < x < 0.4. The lattice parameter a does not depend on x, whereas c increases with increasing Pd content up to x ¼ 0.2, the palladium solubility limit. The transition from ferromagnetism (TC ¼ 4.25 K) to superconductivity (Tsc ¼ 2.4 K) was observed only for the parent Y9Co7 compound. For the lowest tested Pd doping level (x ¼...

The synthesis, structural, magnetic, thermal, and transport properties are reported for polycrystalline PrIr3. At room temperature PrIr3 displays the rhombohedral space group R-3m and a PuNi3-type structure. At around 70 K a phase transition to a monoclinic C2/m structure is observed and continued cooling reveals temperature independent behavior of the unit cell volume. Further, PrIr3 undergoes a paramagnetic to ferromagnetic transition with...

The ac magnetic susceptibility of a single crystal sample of the compound Y9Co7 has been measured in applied dc fields ranging from 0–6.7 kOe by utilizing a tunnel diode resonator circuit. In agreement with previous measurements on this material, a superconducting transition has been observed to occur at TSC ≈ 2.5 K. A broad maximum has been observed in the zero field susceptibility measurements from 2.5 K < T < 8 K and its behavior...

We present the synthesis and experimental characterization of the binary intermetallic compound Pr7Ru3. The polycrystalline sample was prepared by arc melting pure Pr and Ru, followed by homogenization at 500 °C and 600 °C for 48 and 89 h, respectively. Powder x-ray diffraction confirms that Pr7Ru3 crystallizes in an orthorhombic crystal structure (Pnma, space group no. 62) with the lattice parameters: a = 7.3606(7) Å, b = 23.120(1)...