Degradation of material caused by impacts of a solid particle (erodent) suspended in a liquid is called slurry erosion and is a major problem in the hydropower and maritime industry. Slurry erosion depends on many factors, e.g. liquid and erodent velocity, size, shape, angle of impact, hardness and number of erodents, and strength of a target material. The various types of test devices have been designed to investigate an effect...

In the present work, the slurry erosion tests were carried out to investigate the influence of heat treatment on slurry erosion process of ferritic X10CrAlSi18 stainless steel using a slurry pot test rig. X10CrAlSi18 stainless steel was tested in as-received condition and after annealing at three different temperatures: 600°C, 800°C and 1000°C. Degradation of materials due to slurry erosion depends on many factors connected with...

S235JR steel is used in many applications, but its resistance to the erosion processes has been poorly studied. To investigate this resistance, cavitation, and slurry erosion tests were conducted. These tests were carried out at different erosion intensities, i.e., different flow rates in the cavitation tunnel with a system of barricades and different rotational speeds in the slurry pot. The steel was tested as-received and after...

The degradation of materials due to slurry erosion is the serious problem which occurs in the power industries. The paper presents actual knowledge about an influence of individual factors connected with flow conditions, particles and material properties on the slurry erosion resistance. Among the factors connected with operating conditions, an influence of impact angle, and velocity of impact, particle concertation and liquid...