Szymon Królak
Zatrudnienie
- w Gdansk University of Technology
Obszary badawcze
Publikacje
Filtry
wszystkich: 3
Katalog Publikacji
Rok 2024
-
Detailed studies of superconducting properties of Y2Pd1.25Ge2.75
PublikacjaWe report a successful synthesis of a high-purity intermetallic germanide Y2Pd1.25Ge2.75, crystallizing in the disordered variant of the AlB2-type structure. A single-phase sample was obtained via arc-melting by deliberately tuning the composition out of the ideal 2:1:3 ratio. Specific heat, electrical resistivity and magnetization measurements show that the compound is a weakly-coupled (λ e-p = 0.58) type-II superconductor with...
Rok 2023
-
Superconductivity of Ta-Hf and Ta-Zr alloys: Potential alloys for use in superconducting devices
PublikacjaThe electronic properties relevant to superconductivity are reported for bulk Ta-Hf and Ta-Zr body centered cubic alloys, in a large part to determine whether their properties are suitable for potential use in superconducting qbits. The body centered cubic unit cell sizes increase with increasing alloying. The results of magnetic susceptibility, electrical resistivity, and heat capacity characterization are reported. While elemental...
Rok 2022
-
Ferromagnetism in Pr-rich binary Pr7Ru3 intermetallic compound
PublikacjaWe present the synthesis and experimental characterization of the binary intermetallic compound Pr7Ru3. The polycrystalline sample was prepared by arc melting pure Pr and Ru, followed by homogenization at 500 °C and 600 °C for 48 and 89 h, respectively. Powder x-ray diffraction confirms that Pr7Ru3 crystallizes in an orthorhombic crystal structure (Pnma, space group no. 62) with the lattice parameters: a = 7.3606(7) Å, b = 23.120(1)...