The XRD pattern of CeO2/10wt.%Ni with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor nitrate solution (betacyclodextrin). The dataset includes 5-90 2 theta degree measurement. Nonreduced. Sintered at 400oC for 4h.
-
The XRD pattern of CeO2/10wt.%Fe prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Fe. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Cu prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Cu. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Cu prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Cu. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Co prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Co. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The morphology of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses measured with AFM
Dane BadawczeThe morphology of as-quenched and heat treated 58(2Bi2O3-V2O5)-42SrB4O7 glasses was measured with the use of atomic force microscope.
-
Thermal properties of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with DSC method
Dane BadawczeThermal properties of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by DSC.
-
Thermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with DSC method
Dane BadawczeThermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by DSC.
-
Thermal properties of ceramic Bi2VO5.5 and strontium–borate glass-ceramics containing crystalites of Bi2VO5.5. measured with DSC
Dane BadawczeThermal properties of ceramic Bi2VO5.5 and strontium–borate glass-ceramics containing Bi2VO5.5 crystallites was measured by DSC.
-
Linear impedance of strontium–borate glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of strontium–borate glass was measured by impedance spectroscopy method.
-
Linear impedance of strontium–borate glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties of strontium–borate glass was measured by impedance spectroscopy method.
-
Chemical composition analysis of the LSNO ceramics
Dane BadawczeThe chemical composition of a series of La-Sb-Nb-O ceramics manufactured by the solid-phase reaction method was analyzed. The samples with a various antimony content were measured by XPS method (OmicronNanotechnology UHV system). Analysis confirmed presence of elements: La, Sb, Nb.
-
XPS analysis of strontium titanate ceramics
Dane BadawczeThe chemical composition of the strontium titanite doped with yttrium and iron ceramic samples was investigated. Samples of Y0.07Sr0.93Ti0.8Fe0.2 were prepared by solid phase reaction and sintered for 24 and 48 hours. Chemical composition was measured by UHV OmicronNanotechnology XPS system. The analysis confirmed the chemical composition of the ceramics...
-
Analysis of the properties of the YSTF ceramics materials before and after reduction
Dane BadawczeThe valence of titanium in reduced YSTF ceramics materials was investigated. Ceramics were reduced by annealing in a hydrogen atmosphere. For comparison unreduced sample was also measured. Valance state was measured by XPS method.
-
The TPO oxidation profile of CeO2/10wt.%Cu with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPR reduction profile of CeO2/10wt.%Cu without BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The XRD pattern of CeO2/10wt.%Mn prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Mn. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Mn prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Mn. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The TPO oxidation profile of CeO2/10wt.%Ni with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPR reduction profile of CeO2/10wt.%Ni without BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Co without BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The XRD diffraction patterns of Sr2Al0.1Fe1.4Mo0.5O6 powder calcined at 1100oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr2Al0.1Fe1.4Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1100oC for 12 h in air.
-
The XRD diffraction patterns of Sr1.9Fe1.4Ni0.1Mo0.5O6 powder calcined at 1100oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr1.9Fe1.4Ni0.1Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1100oC for 12 h in air.
-
The TPO oxidation profile of CeO2/10wt.%Fe with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Fe. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Co with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The XRD pattern of CeO2/10wt.%Ni prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Fe prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Fe. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Ni prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4h in air.
-
The XRD pattern of CeO2/10wt.%Co prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Co. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement.
-
The XRD diffraction patterns of Sr1.9Fe1.5Mo0.5O6 powder calcined at 1100oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr1.9Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1100oC for 12 h in air.
-
The XRD diffraction patterns of La0.3Sr1.7Al0.1Fe1.5Mo0.5O6 powder calcined at 1100oC in air
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr1.7Al0.1Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1100oC for 12 h in air.
-
The XRD diffraction patterns of Sr1.9Fe1.4Ni0.1Mo0.5O6 powder calcined at 1200oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr1.9Fe1.4Ni0.1Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
The TPO oxidation profile of CeO2/10wt.%Ni without BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Co without BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Mn without BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPR reduction profile of CeO2/10wt.%Mn without BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Mn with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Fe with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Fe. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The XRD diffraction patterns of Sr1.9Fe1.5Mo0.5O6 powder calcined at 1200oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr1.9Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
The XRD diffraction patterns of La0.3Sr1.7Fe1.5Mo0.5O6 powder calcined at 1200oC in air
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr1.7Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
The XRD diffraction patterns of La0.3Sr2Al0.1FeMoO6 powder calcined at 1200oC in air
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr2Al0.1FeMoO6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
X-ray diffractometry results of the SrTi0.50Fe0.50O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.50Fe0.50O3-d (STF50) powder after ball milling. The phase composition of the investigated STF50 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.35Fe0.65O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.35Fe0.65O3-d (STF35) powder after ball milling. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.30Fe0.70O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.30Fe0.70O3-d (STF70) powder after ball milling. The phase composition of the investigated STF70 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
The TPR reduction profile of CeO2/10wt.%Ni with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Cu with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Co with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using alumina catalyst - blank
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of blank sample Al2O3 for dry reforming of biogas (60/40 CH4-CO2). The specatra were collected every 1 minute.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CLO catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Ce0.8La0.2O2 nanocatalyst. The specatra were collected every 1 minute.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CLO/Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Ce0.8La0.2O2+10wt.%Cu nanocatalyst. The specatra were collected every 1 minute.