The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1000 deg.C in hydrogen

Description

The (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground in an agate mortar, pressed back into pellets, heated in an oven at 1400 °C for 12 hours and cooled to room temperature at a rate of 5 °C/min. The XRD analysis allowed for determining the phase composition of powders after reduction at 1000 deg.C in hydrogen. 

Dataset file

XRD red 1000.rar
39.2 kB, S3 ETag 17ebcee8ddfe4cfe3e6b3c489db33442-1, downloads: 7
The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

File details

License:
Creative Commons: by 4.0 open in new tab
CC BY
Attribution
File embargo:
2026-04-18
Raw data:
Data contained in dataset was not processed.
Software:
High Score

Details

Year of publication:
2023
Verification date:
2023-03-08
Creation date:
2022
Dataset language:
English
Fields of science:
  • materials engineering (Engineering and Technology)
DOI:
DOI ID 10.34808/me1p-hw75 open in new tab
Funding:
Series:
Verified by:
Gdańsk University of Technology

Keywords

Cite as

Authors

seen 110 times