Effect of austempering temperature on microstructure and cyclic deformation behaviour of multiphase low-carbon steel
Abstract
This paper examined the cyclic deformation behaviour of multiphase low-carbon steel that was subjected to austempering heat treatments at four temperatures (190 °C, 230 °C, 275 °C, and 315 °C) below the martensite start temperature (Ms = 353 °C). The tests were conducted at room temperature, under fully reversed strain-controlled conditions, with strain amplitudes in the range 0.5–1.0%. The microstructure was observed by transmission electron microscopy, and the fracture surfaces were examined by scanning electron microscopy. The steel had a bainite/martensite microstructure, with increasing bainite content for higher austempering temperatures. Irrespective of the tested conditions, it strain-hardened during the first two cycles and then, strain-softened until failure. The austempering temperature did not significantly affect the stress-based, strain-based and energy-based relationships. However, lower austempering temperatures slightly improved the fatigue performance.
Citations
-
3
CrossRef
-
0
Web of Science
-
3
Scopus
Authors (7)
-
X. Y. Long
-
Ricardo Branco
-
Reza Masoudi Nejad
-
Grzegorz Lesiuk
-
Shun-Peng Zhu
-
A. M. Amaro
Cite as
Full text
- Publication version
- Accepted or Published Version
- DOI:
- Digital Object Identifier (open in new tab) 10.1007/s43452-023-00735-2
- License
-
open in new tab
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
Archives of Civil and Mechanical Engineering
no. 23,
ISSN: 1644-9665 - Language:
- English
- Publication year:
- 2023
- Bibliographic description:
- Long X. Y., Branco R., Macek W., Masoudi Nejad R., Lesiuk G., Zhu S., Amaro A. M.: Effect of austempering temperature on microstructure and cyclic deformation behaviour of multiphase low-carbon steel// Archives of Civil and Mechanical Engineering -,iss. 3 (2023),
- DOI:
- Digital Object Identifier (open in new tab) 10.1007/s43452-023-00735-2
- Sources of funding:
-
- Free publication
- Verified by:
- Gdańsk University of Technology
seen 82 times
Recommended for you
Influence of Heat Treatment Temperature on Fatigue Toughness in Medium-Carbon High-Strength Steels
- G. Wheatley,
- R. Branco,
- J. A. F. O. Correia
- + 4 authors
Fractographical quantitative analysis of EN-AW 2024 aluminum alloy after creep pre-strain and LCF loading
- W. Macek,
- A. Tomczyk,
- R. Branco
- + 2 authors
Multiaxial Fatigue Behaviour of SLM 18Ni300 Steel
- R. Branco,
- J. D. Costa,
- J. A. M. Ferreira
- + 3 authors
The effect of elevated temperature on LCF damage growth in 2024AA – Experiment and modeling
- A. Falkowska,
- A. Tomczyk,
- A. Seweryn