Effect of austempering temperature on microstructure and cyclic deformation behaviour of multiphase low-carbon steel
Abstrakt
This paper examined the cyclic deformation behaviour of multiphase low-carbon steel that was subjected to austempering heat treatments at four temperatures (190 °C, 230 °C, 275 °C, and 315 °C) below the martensite start temperature (Ms = 353 °C). The tests were conducted at room temperature, under fully reversed strain-controlled conditions, with strain amplitudes in the range 0.5–1.0%. The microstructure was observed by transmission electron microscopy, and the fracture surfaces were examined by scanning electron microscopy. The steel had a bainite/martensite microstructure, with increasing bainite content for higher austempering temperatures. Irrespective of the tested conditions, it strain-hardened during the first two cycles and then, strain-softened until failure. The austempering temperature did not significantly affect the stress-based, strain-based and energy-based relationships. However, lower austempering temperatures slightly improved the fatigue performance.
Cytowania
-
3
CrossRef
-
0
Web of Science
-
3
Scopus
Autorzy (7)
-
X. Y. Long
-
Ricardo Branco
-
Reza Masoudi Nejad
-
Grzegorz Lesiuk
-
Shun-Peng Zhu
-
A. M. Amaro
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/s43452-023-00735-2
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Archives of Civil and Mechanical Engineering
nr 23,
ISSN: 1644-9665 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Long X. Y., Branco R., Macek W., Masoudi Nejad R., Lesiuk G., Zhu S., Amaro A. M.: Effect of austempering temperature on microstructure and cyclic deformation behaviour of multiphase low-carbon steel// Archives of Civil and Mechanical Engineering -,iss. 3 (2023),
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/s43452-023-00735-2
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 86 razy
Publikacje, które mogą cię zainteresować
Influence of Heat Treatment Temperature on Fatigue Toughness in Medium-Carbon High-Strength Steels
- G. Wheatley,
- R. Branco,
- J. A. F. O. Correia
- + 4 autorów
Fractographical quantitative analysis of EN-AW 2024 aluminum alloy after creep pre-strain and LCF loading
- W. Macek,
- A. Tomczyk,
- R. Branco
- + 2 autorów
Multiaxial Fatigue Behaviour of SLM 18Ni300 Steel
- R. Branco,
- J. D. Costa,
- J. A. M. Ferreira
- + 3 autorów
The effect of elevated temperature on LCF damage growth in 2024AA – Experiment and modeling
- A. Falkowska,
- A. Tomczyk,
- A. Seweryn