Electrical properties of Y0.08Sr0.92Ti0.92Nb0.08O3-δ after reduction in different reducing conditions
Abstract
Electrical properties of perovskite Y0.08Sr0.92Ti0.92Nb0.08O3−ı after reduction in different conditions were studied. Relatively high electrical conductivity in samples reduced in ammonia was observed. The conductivity of Y0.08Sr0.92Ti0.92Nb0.08O3−ı reduced in ammonia at 1500 ◦C was of about 600 S/cm at 200 ◦C. Conductivity after reduction in ammonia at 1500 ◦C was stable both in hydrogen and oxygen atmosphere up to 600 ◦C. Reduction Y0.08Sr0.92Ti0.92Nb0.08O3−ı in ammonia causes nitrogen incorporation into perovskite structure of Y0.08Sr0.92Ti0.92Nb0.08O3−ı.
Authors (8)
-
A. Winiarski
- Uniwersytet Śląski Instytut Fizyki
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuł w czasopiśmie wyróżnionym w JCR
- Published in:
-
JOURNAL OF ALLOYS AND COMPOUNDS
no. 473,
edition 1-2,
pages 496 - 499,
ISSN: 0925-8388 - Language:
- English
- Publication year:
- 2009
- Bibliographic description:
- Karczewski J., Bochentyn B., Molin S., Winiarski A., Gazda M., Jasiński P., Murawski L., Kusz B.: Electrical properties of Y0.08Sr0.92Ti0.92Nb0.08O3-δ after reduction in different reducing conditions// JOURNAL OF ALLOYS AND COMPOUNDS. -Vol. 473, iss. 1-2 (2009), s.496-499
- Verified by:
- Gdańsk University of Technology
seen 99 times