Hydrogen induced degradation of structural steel exposed to the technical liquid hydrocarbons

Beata Świeczko-Żurek; Andrzej Zieliński; Ellina Łunarska

Hydrogen induced degradation of structural steel exposed to the technical liquid hydrocarbons

Abstract

Susceptibility of the differently heat treated 26H2MF steel to stress corrosion cracking has been evaluated in the constant strain rate tension tests done at the strain rate 10-6s-1 and in the constant load tests done at the 0,98 of fracture load. The boiler fuel and the aged mineral oil at 135C and 80C respectively, have been used as the aggressive environments.

Authors (3)

Beata Świeczko-Żurek dr hab. inż.
Andrzej Zieliński prof. dr hab. inż.
- Faculty of Mechanical Engineering
- Gdańsk University of Technology
Ellina Łunarska
- Faculty of Mechanical Engineering
- Gdańsk University of Technology

Cite as

Full text

full text is not available in portal

Keywords

Details

Category:: Conference activity
Type:: publikacja w wydawnictwie zbiorowym recenzowanym (także w materiałach konferencyjnych)
Title of issue:: Problemi koroziï ta protikorozijnogo zahistu materialiv = Problems of corrosion and corrosion protection materials, Lviv, 2006. strony 216 - 221
Language:: English
Publication year:: 2006
Bibliographic description:: Świeczko-Żurek B., Zieliński A., Łunarska E.: Hydrogen induced degradation of structural steel exposed to the technical liquid hydrocarbons// Problemi koroziï ta protikorozijnogo zahistu materialiv = Problems of corrosion and corrosion protection materials, Lviv, 2006./ Lviv: Nacional. Akad. Nauk Ukr., 2006, s.216-221
Verified by:: Gdańsk University of Technology