One of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper an experimental...

In this paper, a comparison of the mechanical properties of high-strength low-alloy S460Nsteel welded joints is presented. The welded joints were made by the gas metal arc welding (GMAW)process in the air environment and water, by the local cavity welding method. Welded joints were testedfollowing the EN ISO 15614-1:2017 standard. After welding, the non-destructive—visual, penetrant,radiographic, and ultrasonic (phased array) tests...

Wire arc additive manufacturing (WAAM) is an additive manufacturing process based on the arc welding process in which wire is melted by an electric arc and deposited layer by layer. Due to the cost and rate benefits over powder-based additive manufacturing technologies and other alternative heat sources such as laser and electron beams, the process is currently receiving much attention in the industrial production sector. The gas...

One of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper the state...

A dissimilar welded joint of Inconel 718 and 304L austenitic stainless steel was prepared using a combined procedure with the gas tungsten arc welding and shielded metal arc welding processes by employing the Ni-based fillers: ERNiCr-3 and ENiCrFe-3. The welded joints were investigated for metallographic testing and mechanical properties, and a relationship was established between the microstructure and the resultant mechanical...