This study presents results of experimental tests on quality of dissimilar welded joints between 316L austenitic and 2304 lean duplex stainless steels, welded without ceramic backing. Fiber laser welded butt joints at a thickness of 8 mm were subjected to non‐destructive testing (visual and penetrant), destructive testing (static tensile test, bending test, and microhardness measurements) and structure observations (macro‐ and...

Great interest of the laser beam welding in industry is a new theoretical task, making planning the welding procedure specification and the quality control of welded joints easier. Estimating and calculating the dimensions of a weld pool and temperature distribution near weld mainly concern heat source modelling. In the presented work calculations of welding pool shape and thermal field for cylindrical-powered-normally model of...

A dissimilar autogenous laser welded joint of AISI 430F (X12CrMoS17) martensitic stainless steel and AISI 304 (X5CrNi18-10) austenitic stainless steel was manufactured. The welded joint was examined by non-destructive visual testing and destructive testing by macro- and microscopic examination and hardness measurements. With reference to the ISO 13919-1 standard the welded joint was characterized by C level, due to the gas pores...

The use of welding processes in the manufacturing and repair of structures intended for the energy industry plays a key role in the guarantee of a continuous supply of fossil fuels, which is the basic condition for ensuring energy security. A square butt joint of 10 mm thick plate of 2.25Cr–1Mo (P22) steel was fabricated by autogenous laser beam welding process and then post-weld heat treatment (PWHT) for two sets of process parameters...

The high entropy alloy (HEA) filler used during the fabrication method determines the reliability of HEAs for steel-aluminum dissimilar alloy configuration. HEAs have a direct impact on the formation of intermetallic compounds (IMC) formed by the interaction of iron (Fe) and aluminum (Al), and influence the size of the joint’s interaction zone. A novel welding process for Fe-Al alloy joints was developed to prevent the development...