W pracy przedstawiono wybrane aspekty niszczenia wodorowego metali oraz złączy spawanych. Przedstawiono stanowiska badawcze wykorzystywane do oceny niszczenia wodorowego, w tym zaprojektowane i wykonane w Zespole Inżynierii Spajania PG stanowisko do realizacji próby SSRT.

Badano skłonnośc strefy wpływu ciepła spoin ze stali dupleks do korozyjnego pękania narężeniowego. Wykonano próby korozyjne z wykorzystaniem metody SSRT w środowisku korozyjnym wrzącego MgCl2. Wykazano, że duży udział ferrytu w strukturze SWC pogarsza odpornośc na korozję. Badania metalograficzne na mikroskopie lektronowym wykazały różne sposoby propagacji pęknięcia zależnie od zawartości austenitu w strukturze SWC.

The cracking behavior of 2205 duplex stainless steels (DSSs) in synthetic sea water under cathodic polarization condition was investigated. (SSRT) method was employed in aim to evaluate the susceptibility to hydrogen assisted cracking. The results showed that the reduction in the uniform elongation (UEL) and the reduction of area (RA) varied with the applied cathodic current density. Significant reductions in ductility were found,...

This paper presents results of the research on impact of microstructure of austenitic-ferritic steel of duplex type on its mechanical properties and susceptibility to stress corrosion cracking. As showed, improper processing technologies more and more often used in shipbuilding industry for plates and other half-finished products made of duplex steel may cause significant lowering their properties, which frequently makes their...

The paper describes structure and properties of dissimilar stainless steels welded joints between duplex 2205 and austenitic 316L steels. Investigations were focused on environmentally assisted cracking of welded joints. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement was determined in slow strain rate tests (SSRT) with the strain rate of 2.2 × 10–6 s–1. Chloride-inducted SCC was determined in the...