ABSTRACT The present work was conducted to assess the weldability of duplex stainless steel in underwater conditions. Metal manual arc welding (MMA) with the use of coated electrodes was used in the investigations. Tekken weldability tests were performed underwater at 0.5 m depth and in the air. Nondestructive tests, metallographic examinations of welds, ferrite content assessment in microstructure and hardness test were performed....

In this paper, the application possibilities of the ultra-high strength (UHSS). Domex 960 steel in the underwater welded structures are analyzed. In the research, the investigated material has been tested in bead-on-plate wet welding conditions with the usage of different heat input values, namely 0.63 kJ/mm, 0.72 kJ/mm and 0.93 kJ/mm. Specimens were performed by the manual metal arc (MMA) welding method with the usage of rutile...

The participation of high strength steels in marine and offshore structures is increasing, which makes it necessary to develop recommendations for underwater repair welding works. The article presents the results of bead-on-plate welded specimens made of S700MC high strength steel in underwater wet welding conditions by covered elec- trodes. Three specimens with heat input values in the range 0.91-1.05 kJ/mm were made. The specimens...

The article describes manufacturing technology of multilayer joints in terms of control the diffusible hydrogen content. Diffusible hydrogen content in deposited metal for multilayer welded joints made of covered rutile electrodes or covered cellulosic and basic electrodes was determined. It was found that after four beads, the diffusible hydrogen content decreases in the case of the first technology from 36 ml/100 g to 18 ml/100...

The determination of diffusible hydrogen content in deposited metal of P 62 MR covered electrodes for manual metal arc welding by mercury method was carried out. The test results indicate that covered electrodes 62 P MR grade generate a mean of 4.02 ml/100g of diffusible hydrogen in deposited metal, which is consistent with H5 class.