This paper presents the results of oxidation and corrosion tests carried out on titanium alloy Ti13Nb13Zr. The oxide film was prepared by electrochemical environment 2M H3PO4 for 30 min and 1 h, at a constant voltage 40V. The tests of corrosion resistance were performed by potentiostatic method in Ringer's solution at different pH values: 7, 5 and 3. The change in an appearance of surface and the increase in corrosion resistance...

The development of composite oxide layers on the Ti13Nb13Zr alloy, their structure and properties have been demonstrated. Two subsequent methods were applied to prepare the composite layers. During the first stage gas oxidation produced a solid oxide layer, and subsequently oxide nanotubes were produced by using an electrochemical method. Scanning electron microscopy (SEM), chemical analysis, energy dispersive X-ray spectroscopy...

The Ti13Nb13Zr alloy was subjected to laser modification with the Nd:YAG laser provided that such treatment would increase the surface roughness followed improved adhesion of hydroxyapatite (HAp) coatings The hydroxyapatite was deposited by electrophoretic method in suspension of 0.5 g HA powder and 100 ml ethyl alcohol. The deposition was carried out for 10 min at 10 V voltage followed by drying at room temperature for 24 h and...

Przeprowadzono badania materiału porowatego, przeznaczonego na implanty ortopedyczne, wytworzonego metodą metalurgii proszków ze stopu Ti13Nb13Zr. Proszki z badanego stopu uzyskano metodą rozpylania plazmowego. Otrzymano próbki o otwartej porowatej strukturze, stopniu porowatości do 68% i średniej wielkości porów w przedziale 30-150 mikrometrów. Obróbka próbek porowatych - utlenianie termiczne, chemiczne i/lub elektrochemiczne...