W pracy dokonano analizy protokołu kryptograficznego nazwanego ''metoda szyfrowania ZT-UNITAKOD'' i zaproponowanego przez Zygmunta Topolewskiego. Autor metody twierdzi, że zaproponował metodę szyfrowania nie wymagającą klucza. W pierwszej części pracy przedstawiono opis metody i wariantów niektórych proponowanych algorytmów szyfrowania. W drugiej części przeprowadzono analizę protokołu kryptograficznego zaproponowanego w opisie...

This paper presents a proposal of simultaneous consideration of load and wear associated with it , of tribological systems of ship main engines (intended for ship propulsion) . Based on results of investigations it was assumed that both the load Q (i.e. a cause of wear ) and the wear Z (i.e. an effect of load occurrence) considered in a given time t(0 ≤ t ≤ t) are random variables Qt and Zt, respectively. There was characterized...

Highly porous, In-filled CoSb3 skutterudite materials with an attractive thermoelectric figure of merit (ZT * 1) and corresponding dense samples were fabricated through the cost-effective method of reduction in oxides in dry hydrogen and the pulsed electric current sintering (PECS) method, respectively. The reduction process was described in detail using in situ thermogravimetric analysis of Co2O3, Sb2O3 and In(NO3)35H2O separately...

A novel method for thermoelectric materials fabrication using a reduction of oxide precursors in hydrogen was reported. On the example of Bi-Sb, Bi-Sb-Te and Te-Ag-Ge-Sb compounds it was shown that this simple and easy method is suitable for fabrication of two-, three- and even multicomponent thermoelectric materials. It allows controlling a composition, microstructure and even type a of electrical charge carriers. As a result...

The Ge0.77Ag0.1Sb0.13Te1alloy was fabricated by a novel two step route. For that purpose firstly the oxide reagents were melted at high temperature and quenched into pellets. After that pellets were milled to the powder and then reduced in hydrogen at various temperatures and for various periods of time. Energy dispersive X-ray analysis indicated the possibility of successful fabrication of stoichiometric thermoelectric materials...