TEM and EDX study of the Al2O3 ultra thin films
Open Research DataThe ultra-thin layers of Al2O3 were deposited on a silicon substrates. The method of atomic layer deposition (Beneq TFS 200 ALD system) was chosen as the proper method of dielectric layer deposition. This method provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water....
-
XPS measurements of the iron elements covered by chromium
Open Research DataAnticorrosive coatings are an important issue in modern materials engineering. One of the most commonly used, for that coating materials, is chrome. Three metal elements were measured, named as Turcja, WB Tech and Nomet. Names were given according to producer of elements. XPS measurements of the Cr 2p region give an ansver concering on surface chemical...
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 473 K for 3 h measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 473 K for 3h was measured by impedance spectroscopy method.
-
Linear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of as-quenched 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 400°C under argon atmosphere
Open Research DataThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 400°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Linear impedance of V2O5 nanorods obtained at 893K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 903K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 913K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 923K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Non-linear impedance of V2O5 nanorods obtained at 923K
Open Research DataThe DataSet contains the non-linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
XRD patterns of VO2 and V2O3 thin films obtained at 500°C
Open Research DataThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon atmosphere.
-
XRD patterns of VO2 and V2O3 thin films obtained at 700°C
Open Research DataThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (5-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon atmosphere.
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C dependent on film thickness
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (2-3 AsP layers) were deposited on a silicon substrate and were annealing at 1000°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films were deposited on a silicon and quartz glass substrate and were annealing at 1000°C under an argon atmosphere.
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 500°C
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 700°C
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon...
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Open Research DataThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
Powder x-ray diffraction pattern of polycrystalline synthetic leningradite, PbCu3V2O8Cl2
Open Research DataPolycrystalline sample of Cu2+ (S=1/2) antiferromagnetic PbCu3V2O8Cl2 (synthetic analogue of the mineral leningradite) was prepared by solid state reaction of PbCl2, CuO, and V2O5.
-
Powder x-ray diffraction pattern of polycrystalline Cu(IO3)2*xH2O
Open Research DataHydrated copper(II) iodate sample was prepared in water solution by reacting copper(II) sulfate and potassium iodate, following the method described by Peterson (J. Chem. Educ. 1957, 34, 12, 612). The sample was subsequently dried at various temperatures in order to produce an anhydrous Cu(IO3)2:
-
Electrical measurements of the dewetting of metal thin films
Open Research DataIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...
-
Sol-gel derived TeO2:RE powders
Open Research DataTellurium dioxide powders doped by Europium or Dysprosium were prepared by sol-gel method. Samples were annealed in ix of Ar and O2 atomosphere at 600 degrees. Presence of rare earth dopants and Te4+ phase was confirmed by X-Ray Photoemission Spectroscopy method (XPS). For XPS measurements samples with 1 atomic % and 5 atomic % of dopand were selected.
-
XPS study of the NH4-VOx powders
Open Research DataVanadium pentoxide samples were prepared by sol-gel method. The starting solution was prepared by mixing vanadium (V) oxytripropoxide (Aldrich) in an anhydrous ethanol as solvent and acetylacetone. By drying the sol at 323 K for 48 h, it transforms via gel into a xerogel powder. Next, the precursor powder was pressed into the disk-shaped pellets. Samples...
-
Hydrogenation process ofTiO2/BiVO4/PEDOT:PSS observed by XPS method
Open Research DataTitania nanotubes synthesis was based on a two-stage anodization process at water/ethylene glycol (5%/95%) electrolyte containing 0.27 M NH4F and 1 M H3PO4 described previously. Anodization process was performed in two-electrode cell compartment using platinum mesh as a cathode. The distance between electrodes was about 2 cm. The anodization voltage...
-
Chemical investigations of the MoO3 doped by K films deposited FTO
Open Research DataMoO3 thin films were synthesized via thermal annealing of thin, metallic Mo films deposited onto the FTO substrate using a magnetron sputtering system. The influence of photointercalation of alkali metal cation (K+) into the MoO3 structure on the photoelectrochemical properties of the molybdenum trioxide films was investigated. The chemical characterisation...
-
Depth chemical profile in a CeIr3 sample
Open Research DataThe polycrystalline sample of CeIr3 used in the present studies was synthesized by arc-melting cerium (4N) and iridium (3N5) in an arc furnace on a water-cooled copper hearth using a tungsten electrode under a high purity argon atmosphere. A piece of zirconium was used as an oxygen getter. First, a button of Ir was prepared by arc-melting the iridium...
-
XPS investigations of tge tin/tin oxides - CNT composites
Open Research DataThe composite of tin/tin oxide nanoparticles with graphene oxide and CMC based on laser ablation technique as an electrode material for energy storage devices were manufactured. The material exhibited a three-dimensional conducting graphene oxide network decorated with tin or tin oxide nanoparticles. The presence of tin/tin oxide in composites was...
-
SPTNO ceramics measured by XPS method
Open Research DataSPTNO (Sr-Pr-Ti-Ni-O) ceramic were manufactured by solid state reaction, from oxides compounds. Synthesis conducted in air atmosphere at temperature in a range of 800-900 deg. Chemical composition of prepared materials were measured by XPS (X-Ray photoemision spectroscopy) method. UHV OmicronNanotechnology system with 128 channel Argus hemispherical...
-
SEM inwestigation of the silver nanostructures
Open Research DataSilver thin films with a thickness of 1nm, 3nm, 5nm, 7nm and 9nm were deposited by a table-top magnetron sputtering unit in a pure argon plasma from a high-purity silver target. Silicon wafers was used as a substrates. As-deposired films were annealed in Ar atmosphere at 550 Celsius degree for 15 minutes.As a result of annealing, Ag nanostructures formed...
-
Luminescence and FTIR measurements of B2O3-Bi2O3-SrF2 glass and glass-ceramics doped with Eu3+ ions
Open Research DataLuminescence and FTIR measurements of B2O3-Bi2O3-xSrF2+2Eu (x=10,20) glass and glass-ceramics. The emission and excitation spectra of the samples depend on the composition and annealing time.
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method
Open Research DataThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 25xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XPS spectra of ZrO2/5%Cu prepared using wet impregnation method
Open Research DataThe dataset includes XPS spectra of ZrO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
FTIR spectra of gas mixtures from the methanation chamber filled with 25-75wt.% NiO-Al2O3
Open Research DataThe dataset includes the FTIR spectra collection of the outlet gas mixtures (CO2, CO, CH4) from reactor chamber filled with 25/75 wt.% NiO-Al2O3 catalyst for perfoming methanation reaction. The inlet gas mixture was composed of 3:1 by vol. H2:CO. Spectra were collected using PerkinElmer FTIR every 1 min.
-
FTIR spectra of gas mixtures from the methanation chamber filled with 50-50wt.% NiO-GDC
Open Research DataThe dataset includes the FTIR spectra collection of the outlet gas mixtures (CO2, CO, CH4) from reactor chamber filled with 50/50 wt.% NiO-GDC (Gadolinia Doped Ceria 20mol.%Gd2O3) catalyst for perfoming methanation reaction. The inlet gas mixture was composed of 3:1 by vol. H2:CO. Spectra were collected using PerkinElmer FTIR every 1 min.
-
The XPS spectra of SrTiO3/5%Cu prepared using wet impregnation method
Open Research DataThe dataset includes XPS spectra of SrTiO3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of Al2O3/5%Cu prepared using wet impregnation method
Open Research DataThe dataset includes XPS spectra of Al2O3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The TPR reduction profile of MCO powder
Open Research DataThe dataset includes the TPR reduction profiles of MnCo2O4 (MCO) commercial powder. The dataset includes a cycle of reduction under H2/Ar mixture from 100C to 900C. Gas flow:40ml/min and temperature ramp: 10deg/min. Degassed at 200C in He for 1 h.
-
FTIR spectra of gas mixtures from the methanation chamber filled with 50-50wt.% NiO-Al2O3
Open Research DataThe dataset includes the FTIR spectra collection of the outlet gas mixtures (CO2, CO, CH4) from reactor chamber filled with 50/50 wt.% NiO-Al2O3 catalyst for perfoming methanation reaction. The inlet gas mixture was composed of 3:1 by vol. H2:CO. Spectra were collected using PerkinElmer FTIR every 1 min.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CeO2/5%Cu catalyst
Open Research DataThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using CeO2/5%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method - 50xCMC
Open Research DataThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 50xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using modified Pechini/EDTA method
Open Research DataThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using modified Pechini method consisting of CA (citric acid), PEG (propylene glycol) and EDTA. Exact amount of metal nitrates were dissolved in water followed by addition of gelling agents and heated to 100C. Obtained gel was calcined at 600C for 4h. The powder...