- PhD Student at Institute of Nanotechnology and Materials Engineering
seria: Data used in article "Influence of iron content on water uptake and charge transport in BaCe0.6Zr0.2Y0.2−xFexO3−δ triple-conducting oxides" liczba: 4
expand collapse-
Thermogravimetric analysis data of hydration in air for BaCe0.6Zr0.2Y0.2-xFexO3-δ (x = 0, 0.02, 0.05, 0.1)
Open Research DataThe dataset consists of 6 files of thermogravimetric analysis (TGA) data. The TGA experiments of hydration for BaCe0.6Zr0.2Y0.2O3-δ (BCZY622), BaCe0.6Zr0.2Y0.18Fe0.02O3-δ (BCZYFe2), BaCe0.6Zr0.2Y0.15Fe0.05O3-δ (BCZYFe5), and BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe10) were conducted on Netzsch STA 449.
-
Iodometric titration analysis for BaCe0.6Zr0.2Y0.2-xFexO3-δ (x = 0.02, 0.05, 0.1)
Open Research DataThe determination of oxygen nonstoichiometry in the series of BaCe0.6Zr0.2Y0.2-xFexO3-δ (x = 0.02, 0.05, 0.1) compounds was carried out using the iodometric titration method.
-
Electrochemical impedance spectroscopy measurements - conductivity vs. temperature and conductivity vs. oxygen partial pressure for BaCe0.6Zr0.2Y0.2-xFexO3-δ (x = 0.02, 0.05, 0.1)
Open Research DataThe dataset consists of two main catalogs consisting of measurement data: of the electrical conductivity of the BaCe0.6Zr0.2Y0.18Fe0.02O3-δ (BCZYFe2), BaCe0.6Zr0.2Y0.15Fe0.05O3-δ (BCZYFe5), and BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe10) samples as a function of temperature and of the electrical conductivity as a function of oxygen partial pressure (pO2)....
-
Electrical conductivity relaxation measurements - water uptake and oxidation of BaCe0.6Zr0.2Y0.2-xFexO3-δ (x = 0.02, 0.05, 0.1)
Open Research DataThe dataset consists of 2 main catalogs: measurements performed for oxidation/reduction (Oxidation) and hydration/dehydration (Hydration). Each of them consists individual catalogs for the measurements performed on the samples indicated by the name of the catalog. In the case of oxidation/reduction, inside each them, there are catalogs indicating if...
-
The electrical conductivity of pristine, La-, and Nb-doped SFM measured in air and hydrogen atmospheres
Open Research DataThis dataset consists of an Excel sheet with the result of DC4W method of electrical measurements. The measurements were conducted on pristine strontium ferrite molubdate as well as ones doped with La and Nb. Additionally two samples co-doped with La and Ni/Co were analyzed. Pellets were prepared by high temperature sintering at 1400 deg. C, then cut...
seria: Data used in article "Water uptake kinetics and electrical transport in BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Tb, Pr, Fe) protonic conductors" liczba: 5
expand collapse-
Thermogravimetric analysis data of hydration in air and nitrogen for BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Open Research DataThe dataset consists of 6 files of thermogravimetric analysis (TGA) data. The TGA experiments of hydration for BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were conducted on Netzsch STA 449.
-
X-ray diffraction patterns of BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Open Research DataThe dataset consists of three raw X-ray diffraction (XRD) files collected using a Phillips X’Pert Pro diffractometer (CuKα radiation (𝜆 = 1.541 Å), under 40 kV and 30 mA). The diffraction patterns of BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were collected at room temperature. Collected...
-
Electrical conductivity relaxation measurements - oxidation and reduction of BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Open Research DataThe dataset consists of 2 main catalogs: measurements performed for oxidation/reduction in dry conditions and in humid conditions. For Electrical Conductivity Relaxation (ECR) measurements, platinum reversible electrodes were applied in a four-probe arrangement and the sample was measured in the ProboStat™ measurement system. The ECR measurements were...
-
Electrical conductivity relaxation measurements - water uptake of BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Open Research DataFor Electrical Conductivity Relaxation (ECR) measurements, platinum reversible electrodes were applied in a four-probe arrangement and the BaCe0.6Zr0.2Y0.1Tb0.1O3-δ sample was measured in the ProboStat™ measurement system. The ECR measurements were performed in air in the temperature range of 450-800 ℃ after switching water partial pressure between...
-
Electrochemical impedance spectroscopy measurements - conductivity vs. temperature and conductivity vs. oxygen partial pressure - BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Open Research DataThe dataset consists of two main catalogs consisting of measurement data: of the electrical conductivity of the BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) sample as a function of temperature and of the electrical conductivity as a function of oxygen partial pressure (pO2). Measurements as a function of temperature were carried out in dry and wet air (pH2O ~...