Linear impedance as a function of A.C. voltage for 50(2Bi2O3-V2O5)-50SrB4O7 glass measured with impedance spectroscopy method

Description

The linear electrcial properties as a function of A.C. voltage for 50(2Bi2O3-V2O5)-50SrB4O7 glass was measured by impedance spectroscopy method. 

 The polycrystalline strontium–borate, SrB4O7 was synthesized via a solid state reaction route that involved heating stoichiometric mixtures of analytical grade SrCO3 and H3BO3 at 1073 K for 12 hours. Next, sample of a composition of 50(2Bi2O3-V2O5)-50SrB4O7 (in %mol) was prepared from reagent-grade Bi2O3, V2O5 and preprepared SrB4O7. Samples of glass were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at 1373 K for 2 hours. The melt was poured onto a preheated (573 K) brass plate and pressed by another plate to obtain flat circular disks of 1–2 mm thickness and 20–30 mm in diameter.

 For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the frequency range from 1 mHz to 1 MHz and with the A.C. voltage range from 0.01 Vrms to 3 Vrms, at room temperature with Concept 40 broadband dielectric spectrometer.

Dataset file

set66.zip
14.6 kB, S3 ETag 3f603b2cf23371aa7cbc5f3611c5600c-1, downloads: 28
The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5
download file set66.zip

File details

License:
Creative Commons: by 4.0 open in new tab
CC BY
Attribution
Raw data:
Data contained in dataset was not processed.

Details

Year of publication:
2021
Verification date:
2021-06-21
Dataset language:
English
Fields of science:
  • materials engineering (Engineering and Technology)
DOI:
DOI ID 10.34808/q2ra-xq30 open in new tab
Verified by:
Gdańsk University of Technology

Keywords

References

Cite as

seen 74 times