Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region
Description
The linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K was measured by impedance spectroscopy method.
The polycrystalline strontium–borate, SrB4O7 was synthesized via a solid state reaction route that involved heating stoichiometric mixtures of analytical grade SrCO3 and H3BO3 at 1073 K for 12 hours. Next, sample of a composition of 50(2Bi2O3-V2O5)-50SrB4O7 (in %mol) was prepared from reagent-grade Bi2O3, V2O5 and preprepared SrB4O7. Samples of glass were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at 1373 K for 2 hours. The melt was poured onto a preheated (573 K) brass plate and pressed by another plate to obtain flat circular disks of 1–2 mm thickness and 20–30 mm in diameter. Glass was heat-treated at 613 K with low heating rate.
For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the frequency range from 1 mHz to 1 MHz and the temperature range from 373 K to 613 K, with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer and a high temperature Controller Novotherm HT 1600.
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2015
- Verification date:
- 2021-06-21
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/6848-cx96 open in new tab
- Verified by:
- Gdańsk University of Technology
Keywords
References
- publication Electronic and ionic relaxations in strontium-borate glass and glass-ceramics containing bismuth and vanadium oxides
- publication STRUKTURA ORAZ WŁAŚCIWOŚCI ELEKTRYCZNE MATERIAŁÓW SZKLISTYCH ZAWIERAJĄCYCH GRANULE FERROELEKTRYKA Bi2VO5,5
Cite as
Authors
seen 79 times