Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region

Description

The linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass was measured by impedance spectroscopy method.

The polycrystalline strontium–borate, SrB4O7 was synthesized via a solid state reaction route that involved heating stoichiometric mixtures of analytical grade SrCO3 and H3BO3 at 1073 K for 12 hours. Next, sample of a composition of 50(2Bi2O3-V2O5)-50SrB4O7 (in %mol) was prepared from reagent-grade Bi2O3, V2O5 and preprepared SrB4O7. Samples of glass were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at 1373 K for 2 hours. The melt was poured onto a preheated (573 K) brass plate and pressed by another plate to obtain flat circular disks of 1–2 mm thickness and 20–30 mm in diameter.

For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the frequency range from 1 mHz to 1 MHz and the temperature range from 153 K to 423 K, with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer.

Dataset file

set65.zip

268.9 kB, S3 ETag 1e9853e40ff9042e79977afc717538ed-1, downloads: 32

The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

download

File details

License:: open in new tab

CC BY

Attribution
Raw data:: Data contained in dataset was not processed.

Details

Year of publication:

2015

Verification date:

2021-06-21

Dataset language:

English

Fields of science:

materials engineering (Engineering and Technology)

DOI:

10.34808/n2rh-5675

Verified by:

Gdańsk University of Technology

Keywords

References

Cite as

Authors

seen 83 times

Search