PeopleI am a Faculty member (Associate Professor, Highway and Transportation Research Department) at the Faculty of Civil and Environmental Engineering, Gdansk University of Technology, Poland).My main research interests include: pavement structures, interlayer bonding, pavement materials, recycling of road pavements, asphalt mixtures, bitumens, construction and maintenance of pavement structures.My lectures at the University include:...
-
Investigation of low-temperature cracking in newly constructed high-modulus asphalt concrete base course of a motorway pavement
PublicationThe paper presents the issue of low-temperature transverse cracks which have developed in newly constructed base courses made of high-modulus asphalt concrete mix (HMAC). Numerous transverse cracks developed in the analysed HMAC base during the winter season before the pavement was actually completed, both at the transverse joint locations and in the areas between them. This had not happened so far on such a scale during road construction...
-
Dawid Ryś dr hab. inż.
PeopleCourses PRINCE2® Foundation Certificate in Project Management Tire-Pavement Interaction course Micromechanical Analysis of Asphalt Concrete
-
Właściwości niskotemperaturowe betonów asfaltowych o wysokim module sztywności (AC-WMS) w badaniach trzypunktowego zginania
PublicationArtykuł przedstawia właściwości niskotemperaturowe betonów asfaltowych o wysokim module sztywności. Przedstawione wyniki zostały uzyskane w dwóch badaniach zginania trzypunktowego próbek belkowych: ze stałą prędkością przemieszczenia oraz pod stałym obciążeniem. Obie te metody są od dawna stosowane na Politechnice Gdańskiej do oceny właściwości niskotemperaturowych betonów asfaltowych. Badaniu poddano pięć betonów asfaltowych –...
-
Wpływ zbrojenia polimerowymi włóknami rozproszonymi na wybrane właściwości mieszanek mineralno-asfaltowych
PublicationW artykule przedstawiono wybrane wyniki badań mieszanek mineralno-asfaltowych zbrojonych polimerowymi włóknami rozproszonymi. Ocenie poddano mieszankę włókien zbrojących aramidowo-poliolifenowych pod kątem wpływu ich zastosowania na właściwości niskotemperaturowe i odporności na deformacje trwałe mieszanek mineralno-asfaltowych. Właściwości niskotemperaturowe oceniano na podstawie testu zginania próbek belkowych oraz na podstawie...
-
The Impact of Homogeneity of High Modulus Asphalt Concrete Layer on Low-Temperature Cracking
PublicationDuring winter season of 2012 numerous transverse cracks developed in high-modulus asphalt concrete (HMAC) base of newly constructed motorway. Pavement cracked both in transverse joint locations and in the area between them. Research which was conducted during investigation of the causes and mechanisms of cracking consisted of: field examination, laboratory testing of specimens cored out of the existing pavement, computational analyses...
-
Field Evaluation of High Modulus Asphalt Concrete Resistance to Low-Temperature Cracking
PublicationHigh-modulus asphalt concrete has numerous advantages in comparison to conventional asphalt concrete, including increased resistance to permanent deformations and increased pavement fatigue life. However, previous studies have shown that the construction of road pavements with High Modulus Asphalt Concrete (HMAC) may significantly increase the risk of low-temperature cracking. Those observations were the motivation for the research...
-
Marek Pszczoła dr hab. inż.
PeopleI am a Faculty member (Department of Highway and Transportation Engineering) at the Faculty of Civil and Environmental Engineering, Gdansk University of Technology, Poland). My main research interests include: low-temperature properties of asphalt mixtures, low temperature cracking assessment of pavement structures, road materials properties, thermal stress analysis, design of pavement structures, airfield design and analysis....
-
Field investigation of low-temperature cracking and stiffness moduli on selected roads with conventional and high modulus asphalt concrete
PublicationHigh Modulus Asphalt Concrete (HMAC) was introduced in Poland as a one of the solutions to the problem of rutting, type of deterioration common in the 1990s. After first encouraging trials in 2002 HMAC was widely used for heavily loaded national roads and motorways. However some concerns were raised about low-temperature cracking of HMAC. This was the main reason of the studies presented in this article were started. The article...
-
Comparison of low-temperature cracks intensity on pavements with high modulus asphalt concrete and conventional asphalt concrete bases
PublicationHigh modulus asphalt concrete (HMAC) base courses provide very good resistance to rutting and fatigue but they can increase the risk of low-temperature cracking as compared with conventional asphalt concrete (AC). The article presents the comparison of these two road materials in terms of low-temperature cracking. The statistical method based on the ordered logistic regression model was used. The analysis was based on results of...