Search results for: PARTICLE-REINFORCED MATRIX
-
DYNAMIC MECHANICAL BEHAVIOUR OF GFRP COMPOSITES WITH SiO2 NANO PARTICLES REINFORCED EPOXY MATRIX
PublicationDynamic mechanic (DMA) tests were performed to compare the mechanical behaviour of glass fibre reinforced epoxy laminate composites with SiO2 nanoparticle reinforced matrix. The selection of the most promising nanoparticle concentrations was considered in terms of elastic modulus and glass transition temperature. The reference specimens (0% nanoparticles) did not contain diluent accordingly the results do not allow the exact comparison...
-
<title>Novel matrix for fiber optic chemical sensors made of particle track polymer</title>
Publication -
Submicron inorganic particles as an additional filler in hybrid epoxy matrix composites reinforced with glass fibres
PublicationIn this study, the effect of selected submicron metal oxide (zinc oxide, titanium oxide) or non-metal oxide (silicon dioxide) particles on mechanical and thermo-mechanical properties of epoxy/glass composites was investigated. The applied epoxy resin was a diglycidyl ether of bisphenol-A cured with triethylenetetramine. As a reinforcement twill weave E-glass fabric was used. Hybrid composites (contained particulate and fibrous...
-
Hybrid all-cellulose reinforcement in polypropylene matrix biocomposites for injection moulding - influence of particle geometry and volume fraction on hybrid effect
PublicationThe presented study is focused on evaluation of influence of reinforcement volume fraction and geometry on the occurrence of positive hybrid effect by the hybridisation of man-made cellulose fibres (rayon viscose) with cellulose microparticle fillers applied in polypropylene matrix. Four volume fractions of reinforcement were used at 1:1 combination of short man-made cellulose fibres with cellulose microfillers of different aspect...
-
Effect of mixing method and particle size on hardness and compressive strength of aluminium based metal matrix composite prepared through powder metallurgy route
Publication -
DEGRADATION OF GFRP MARINE LAMINATES WITH NANO PARTICLE MODIFIED COATINGS
PublicationWater absorption and surface blistering behaviour was studied for polyester-matrix laminates with SiO2 nanoparticle reinforced gel coats. Accelerated water immersion tests at 37°C showed that addition of 10% nanoparticles increases blisters incubation time by ca. 50% compared to 5% and 0% nanoparticles composites.
-
Ball on disk test AL(rf.)-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 not treated (reference).
-
Ball on disk test AL(rf.)-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 not treated (reference).
-
Ball on disk test AT4_11-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 TiN powder injected (AT4_11).
-
Ball on disk test AT3_21-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 TiN powder injected (AT3_21).