Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #3)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #1)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #4)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #2)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Calculations of the resistance values of 20 thermistors at 0°C
Open Research DataThe presented data set is part of the research aimed at determining the actual characteristics of each thermistor in a package of twenty NTC10k type sensors.
-
Development of conductive porous media as packing materials for biotrickling filter – microbial fuel cell system (BTF-MFC system)
Open Research DataDataset presents values of electrical resistance measured for three developed conductive packimg materials for the application in a BTF-MFC system.