Diffusible Hydrogen Control in Flux Cored Arc Welding Process
PublicationOne of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper an experimental...
-
Diffusible hydrogen management in underwater wet self-shielded flux cored arc welding
PublicationThis article reports the effect of underwater wet welding parameters and conditions on the diffusible hydrogen content in deposited metal for welding with a self-shielded flux cored wire. The diffusible hydrogen content in deposited metal was determined using the glycerin method according to the Plackett-Burman design determining the significance of the effect of the stick out length, welding current, arc voltage, travel speed...
-
Effect of Storage Conditions of Rutile Flux Cored Welding Wires on Properties of Welds
PublicationThe influence of storage locations of two grades of rutile flux cored welding wires on their surface condition and the strength of the welds made with them were studied. Wires were stored in real urban conditions (Gdańsk and Katowice) for 1 month, simultaneously recording changes in conditions: temperature and relative humidity of the environment. Visual tests of wires in the delivered and stored condition as well as visual and...
-
Storage of High-Strength Steel Flux-Cored Welding Wires in Urbanized Areas
PublicationThe condition of the consumables is a key factor determining the waste reduction in the welding processes and the quality of the welded joint. The paper presents the results of tests of four types of fux-cored wires dedicated for welding high-strength steels, stored for 1 month and 6 months in Poland in two urbanized areas: in a large seaside city (Gdańsk) and in Warsaw, located in the center of the country. The wires were subjected...
-
Exploring the trends in flux-cored arc welding: scientometric analysis approach
PublicationFlux-cored arc welding (FCAW) is a universal group of welding methods in terms of the scope of application and automation possibilities, the share of which in various industries in many countries is still increasing. The paper presents the results of bibliographic analyses (scientometric analysis with the use of VOSviewer, Bibliometrix and CitNetExplorer tools) of a data set of 993 publications indexed in the Web of Science database...
-
Effects of Storing Flux-Cored Wires under Various Conditions
PublicationWelding processes involving the use of flux-cored wires are becoming increasingly popular, particularly in shipbuilding as well as in off-shore and civil engineering. The article presents characteristics of the welding process, its areas of application as well as advantages and disadvantages (e.g. necessity of ensuring appropriate conditions for the storage of filler metal wires). The satisfaction of quality-related requirements...
-
Preliminary studies of seamless flux cored wires stored in extreme conditions
PublicationIn the paper preliminary experimental studies of flux cored wires moisturized under controlled conditions are described. Three seamless wires of different grades have been placed in environmental chamber and moisturized in extremely adverse conditions (temperature T = 60° C, relative humidity H = 90%) for 240 hours. During this time measurements of weight gain and observations of surface of wires have been carried out. Also diffusible...
-
Plasticity of Bead-On-Plate Welds Made with the Use of Stored Flux-Cored Wires for Offshore Applications
PublicationExtreme atmospheric conditions in the marine and offshore industry are harmful to engineering materials, especially to welded joints, and may cause degradation of their properties. This article presents the results of research on the plasticity of bead-on-plate welds made using two types of seamless, copper plated flux-cored wires. Before welding, spools with wire were stored for 1 month in two distinct locations with different...
-
Assessment of absorbability of seamless flux cored wires stored in extreme conditions
PublicationWater absorption tests by gravimetric method of three specimens of seamless rutile flux cored wires for flux cored arc welding were carried out. Examined wires are characterized by varied absorbability (Wg is ranged from 0.03 to 0.11% after 200 h of moisturizing).
-
The Effect of Welding Conditions on Mechanical Properties of Superduplex Stainless Steel Welded Joints
PublicationThe tests results of superduplex stainless steel welded joints made with a different heat input, using automatic submerged arc welding (SAW) and semi-automatic flux-cored arc welding (FCAW) have been presented. Metallographic examinations, the measurements of the ferrite content, the width of the heat affected zone (HAZ) and the hardness of the welds in characteristic areas have been performed. Significant differences in the amount of...
-
Hydrogen embrittlement of X2CrNiMoCuN25-6-3 super duplex stainless steel welded joints under cathodic protection
PublicationThe effect of cathodic polarization conditions on hydrogen degradation of X2CrNiMoCuN25-6-3 super duplex stainless steel welded joints, obtained using flux cored arc and submerged arc welding methods, was evaluated. Slow strain rate tensile tests of base material and welded specimens, ferrite content measurements, scanning electron microscopy observations, and statistical analysis were performed. It was found that hydrogenation...
-
Corrosion behavior of hydrogen charged super duplex stainless steel welded joints
PublicationThe electrochemical behavior of the weld metal, heat-affected zone (HAZ), and base material of super duplex stainless steel (SDSS) welded joints, made with the application of flux-cored arc welding (FCAW) and submerged arc welding (SAW), were investigated with the use of metallographic examinations (optical microscopy and scanning electron microscopy), potentiodynamic polarization measurements and total hydrogen content determination...
-
Weldability of S500MC Steel in Underwater Conditions
PublicationWet welding with the use of covered electrodes is one of the methods of underwater welding. This method is the oldest, the most economic and the most versatile. The main difficulties during underwater wet welding are: high cooling rates of the joint, the presence of hydrogen in the arc area and formation of hard martensitic structure in the weld. These phenomena are often accompanied by porosity of welds and large number of spatters,...
-
Effect of water salinity on properties of multipass underwater wet manual metal arc welded joints
PublicationThe weldability of steel under the water is limited due to the influence of the environment. Water causes limited visibility, presence of the residual stresses, increasing the cooling rate, and increasing the diffusible hydrogen content in deposited metal, leading to the formation of brittle microstructures in heat-affected zone (HAZ). The paper presents the results of mechanical properties testing of S420G2+M steel welded joints...
-
The effect of pre-hydrogen charging on corrosion behaviour of superduplex stainless steel welded joints
PublicationThe paper presents results of research undertaken to determine the influence of hydrogen on passivity and corrosion resistance of 2507 super duplex stainless steel welded joints. Butt welded joints were made with low heat input using flux corded arc welding (FCAW) method. Coupons of 5.0 x 5.0 mm were cut from the welded joints containing weld metal (WM), heat affected zone (HAZ) and parent metal (PM). Hydrogen was introduced...
-
Spawalność ferrytyczno-austenitycznej stali odpornej na korozję typu dupleks 2205 w warunkach podwodnych
PublicationPraca dotyczy problemów spawalności stali odpornej na korozję typu dupleks w warunkach spawania mokrego elektrodami otulonymi i lokalną komorą suchą. Całość rozprawy składa się z dwóch części. Część pierwsza to przegląd literatury, w którym omówiono główne problemy wynikające z przeniesienia procesu spawania pod wodę oraz sposoby minimalizowania negatywnego wpływu środowiska. Część druga jest częścią doświadczalną, zawiera tezę...
-
Effect of shielded electrode wet welding conditions on diffusible hydrogen content in deposited metal
PublicationWet welding is the most popular method of joining in water enviroment. During underwater welding, the weldability of steel is limited by the higher cooling rates and hydrogen content in weld metal. Article presents results of preliminary tests on the effects of wet welding conditions on diffusible hydrogen amount. Seven parameters were optimized using a Plackett-Burman plan to get the most relevant variables. These parameters were:...
-
Effect of underwater local cavity welding method conditions on diffusible hydrogen content in deposited metal
PublicationOne of the methods with great potential for applications in underwater repairs is local cavity welding. In local cavity method, cooling conditions and diffusible hydrogen amount in weld metal are nearly the same as those existed during welding in the air. This paper presents the results of literature survey and preliminary tests of the effect of local cavity welding conditions on diffusible hydrogen amount in a deposited metal....
-
Effect of underwater wet welding conditions on the diffusible hydrogen content in deposited metal
PublicationIn the study mercury displacement method was used for determination of diffusible hydrogen amount in deposited metal obtained during underwater wet welding with covered electrodes in laboratory conditions according to a two-level full factorial design for three factors. The factors and their levels were chosen among conditions and parameters of welding in accordance with the results of own preliminary studies. A statistical analysis...
-
The Effect of Welding Conditions on Diffusible Hydrogen Content in Deposited Metal
PublicationThe article presents the results of a literature survey and preliminary tests which set out effects of welding conditions on the amount of diffusible hydrogen in deposited metal. Experiments were conducted by using rutile coated electrodes which generate high contents of diffusible hydrogen in deposited metal. The amount of diffusible hydrogen was determined by a glycerin test.Eleven factors were considered: the electrode angle,...