• APPLICATION OF MAGNETIC NANOPARTICLES FOR WATER TREATMENT

  Publikacja

  • D. Marcinkowska (dawniej: D. Dulko)

  - Technical Issues - Rok 2016

  In this study magnetic nanoparticles were fabricated and used for water treatment. Nanoparticles were prepared in two ways. The first one involved NiZn ferrite nanoparticles synthesized by co-precipitation of metal cations with sodium hydroxide at high temperature. The second one featured maghemite nanoparticles was prepared by saltassisted solid-state reaction. Modification and functionalization of nanoparticles surface was investigated....

  Pełny tekst do pobrania w portalu

• Materiały dla jednowarstwowych ogniw paliwowych

  Publikacja

  • P. Winiarz

  - Technical Issues - Rok 2016

  A composite material, which may be further applied as a single layer fuel cell, was synthesizes using solid state synthesis method. Composite consisted of two components. The first was a nanoeramic proton conductor - calcium doped lanthanum niobate. The second one was a nanoceramic semiconductor oxide composed of lithium, nickel and zinc oxides respectively.

  Pełny tekst do pobrania w portalu

• Niobiany ziem rzadkich - właściwości i zastosowania

  Publikacja

  • P. Winiarz

  - Technical Issues - Rok 2016

  Rare earth niobates are a very interesting group of materials. These compound have different properties which could be changes in a wide range by appropriate doping. X-Ray diffraction examinations for some compounds of RE3NbO7 group were shown

  Pełny tekst do pobrania w portalu

Rok 2015

• Influence of reduction process on the structural and mechanical properties of (Pb,Bi)-(Si,Ge)-O oxide glasses

  Publikacja

  • B. Bochentyn

  - Technical Issues - Rok 2015

  The effect of the reduction process in H2 at 380 °C on the microstructure and elemental composition of a glass Bi0.4Pb0.2Si0.4Ox has been investigated. It has been shown that after reduction a clearly separated top layer with a thickness of approx. 50 µm was formed on the surface of the sample. This layer is depleted of oxygen and has higher electrical conductivity than the interior of the glass. It has also been found that some...

  Pełny tekst do pobrania w portalu

• Właściwości mechaniczne tworzywa PET - przegląd literatury

  Publikacja

  • P. Wawrzyniak

  - Technical Issues - Rok 2015

  The article describes the influance of the microstructure and environment conditions on the mechanical properties of PET material. From the microskopic point of view, mechanical and thermal properties of PET material have the biggest influance on orientation and crystallization processes of material. From the macroskopic point of view mechanical properties can be described by parameters derived from strees-strain mechanical answers...

  Pełny tekst do pobrania w portalu

• Wpływ procesu redukcji na właściwości strukturalne i mechaniczne szkieł tlenkowych z grupy (Pb,Bi)-(Si,Ge)-O = Influence of reduction process on the structural and mechanical properties of (Pb,Bi)-(Si,Ge)-O oxide glasses

  Publikacja

  • B. Bochentyn

  - Technical Issues - Rok 2015

  The effect of the reduction process in H2 at 380 °C on the microstructure and elemental composition of a glass Bi0.4Pb0.2Si0.4Ox has been investigated. It has been shown that after reduction a clearly separated top layer with a thickness of approx. 50 µm was formed on the surface of the sample. This layer is depleted of oxygen and has higher electrical conductivity than the interior of the glass. It has also been found that some...

  Pełny tekst do pobrania w portalu