Electrochemical impedance spectra and CV curves of V2O5 nanorods
Dane BadawczeThe DataSet contains the EIS spectra for coin-cells and CV curves with the V2O5 nanorods obtained by the sol-gel method. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were measured using the AUTOLAB 302N potentiostat-galvanostat under Nova software. The EIS measurements were recorded in the frequency range 100 kHz to 10 mHz for...
-
Electrochemical impedance spectra and CV curves of V2O5 nanocrystals
Dane BadawczeThe DataSet contains the EIS spectra for coin-cells and CV curves with the V2O5 nanocrystals obtained by the sol-gel method. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were measured using the AUTOLAB 302N potentiostat-galvanostat under Nova software. The EIS measurements were recorded in the frequency range 100 kHz to 10 mHz...
-
Cycling performances of the V2O5 nanostructures as cathode material in Na-ion batteries
Dane BadawczeThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanostructures with different morphology obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here...
-
Cycling performances of the V2O5 nanorods as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanorods obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 and 2C current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1. The...
-
Cycling performances of the V2O5 nanocrystals as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanocrystals obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 and 2C current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1. ...
-
Cyclic voltammetry curves of the V2O5 nanorods (Na-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanorods obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Na-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
Cyclic voltammetry curves of the V2O5 nanorods (Li-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Li-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Rate performance of the V2O5 nanorods as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanorods obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
-
Rate performance of the V2O5 nanocrystals as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanocrystals obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
wyświetlono 5155 razy