Opis
The DataSet contains the FTIR spectra of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology dependent on the annealing temperature.
The FT-IR spectra were recorded at room temperature while using a Perkin-Elmer spectrometer (model Frontier FTIR MIR/FIR) (Waltham, MA, USA). The FT-IR spectra of the samples that were pressed into KBr pellets with constant measure material concentration (0.5%) were collected in the wavenumber range 4000–400 cm^-1 (mid-IR region) while using the KBr beam splitter.
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count}
gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcieCC BYUznanie autorstwa
- Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2021
- Data zatwierdzenia:
- 2021-06-22
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/r08x-s366 otwiera się w nowej karcie
- Seria:
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Powiązane zasoby
- dane badawcze SEM micrographs of morphology evolution of VO2 and V2O3 nanostructures
- dane badawcze XRD patterns of VO2 and V2O3 nanostructures
- publikacja The influence of thermal conditions on V2O5 nanostructures prepared by sol-gel method
- dane badawcze Thermal behaviour of vanadium xerogel powder under different inert atmosphere
Cytuj jako
Autorzy
wyświetlono 274 razy