Investigation of plasmon resonance in a silver nanoparticles - Open Research Data - MOST Wiedzy

Wyszukiwarka

Investigation of plasmon resonance in a silver nanoparticles

Opis

Silver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident power was in the range of 30–40 W. The layer thickness was measured in situ using a quartz crystal microbalance. To form nanostructures, the as-prepared films were put into a hot furnace and annealed in argon atmosphere at different temperatures for different periods of time. Plasmon resonance was observed in a UV-VIS (Thermo Fisher Scientific Evolution 220 spectrophotometer in transmission mode, in a range of 200–1100 nm) spectroscopy results, as a absorption peak on transmission spectra.

Plik z danymi badawczymi

Ag.zip
59.0 kB, S3 ETag 73a54d4976dd45eb07de21acc6432e00-1, pobrań: 32
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
pobierz plik Ag.zip

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:
origin

Informacje szczegółowe

Rok publikacji:
2021
Data zatwierdzenia:
2021-06-25
Data wytworzenia:
2018
Język danych badawczych:
angielski
Dyscypliny:
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/6qt2-hq69 otwiera się w nowej karcie
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Cytuj jako

wyświetlono 120 razy