Impedance spectroscopy measurements in various gas atmospheres were carried out in order to explain the doubts about the type of carriers and the mechanism of electrical conductivity in Bi-Si-O and Pb-Si-O glasses. In bismuth silicate glass, a typical ionic conductivity with oxygen ions as charge carriers was observed. The level of electrical conductivity of the glass at 400 °C was 5 × 10−8 S·cm−1 , with the activation energy of 1.3 eV and was independent of measuring atmosphere. In the case of lead silicate glasses, the conductivity changed with measuring atmosphere. Two types of charge carriers: oxygen ions and proton ions were postulated. Proton conductivity measured in wet argon at temperature 400 °C was estimated at the level of 4 × 10−8 S·cm−1 while the oxygen ions conductivity in such conditions was 78 × 10−8 S·cm−1 . We suggest that both types of charge carriers are transported along the same conduction paths using oxygen defects in the glass structure.
Cytowania
-
5
CrossRef
-
0
Web of Science
-
6
Scopus
Autorzy (4)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
MATERIALS SCIENCE-POLAND
nr 35,
strony 681 - 686,
ISSN: 0137-1339 - Język:
- angielski
- Rok wydania:
- 2018
- Opis bibliograficzny:
- Karczewski J., Miruszewski T., Bochentyn B., Kusz B.: Determination of ionic conductivity in the Bi-Si-O and Pb-Si-O glasses// MATERIALS SCIENCE-POLAND. -Vol. 35, nr. 4 (2018), s.681-686
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1515/msp-2017-0102
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 175 razy
Publikacje, które mogą cię zainteresować
Electrical properties of Na2O-CaO-P2O5 glasses doped with SiO2 and Si3N4
- N. A. Wójcik,
- B. Jonson,
- R. J. Barczyński
- + 3 autorów