Effective yttrium based coating for steel interconnects of solid oxide cells: Corrosion evaluation in steam-hydrogen atmosphere
Abstrakt
This work describes manufacture, analysis and test of a new well conducting corrosion-protection coating that can be applied on steel types with high chromium content. Electrolytic deposition of yttrium salts is used to form thin (<100 nm) coatings on both flat steel sheets (material: Crofer 22 APU) and its properties are proven on woven wire-meshes (materials from two different sources: SUS316 and SUS316L). The oxide scale on the coated Crofer 22 APU sheet remains intact after 2000 h operation at 750 °C in H2 with 90% H2O. The corrosion rate at 750 °C of the coated Crofer 22 APU sheets is compared with that of uncoated samples and of samples with a commercial magneton sputtered CGO coating revealing that the coatings reduce the parabolic rate constant characteristic of the corrosion by a factor of 10 and 20 for the CGO and the Y, respectively.
Cytowania
-
1 7
CrossRef
-
0
Web of Science
-
1 9
Scopus
Autorzy (9)
-
Å.h. Persson
- Technical University of Denmark Department of Energy Conversion and Storage
-
T.l. Skafte
- Technical University of Denmark Department of Energy Conversion and Storage
-
A.l. Smitshuysen
- Technical University of Denmark Department of Energy Conversion and Storage
-
S.h. Jensen
- Technical University of Denmark Department of Energy Conversion and Storage
-
K. H. Andersen
- Technical University of Denmark Department of Energy Conversion and Storage
-
H. Xu
- Technical University of Denmark Department of Energy Conversion and Storage
-
Ming Chen
- Technical University of Denmark Department of Energy Conversion and Storage
-
Peter Vang Hendriksen
- Technical University of Denmark Department of Energy Conversion and Storage
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
JOURNAL OF POWER SOURCES
nr 440,
ISSN: 0378-7753 - Język:
- angielski
- Rok wydania:
- 2019
- Opis bibliograficzny:
- Molin S., Persson Å., Skafte T., Smitshuysen A., Jensen S., Andersen K., Xu H., Chen M., Hendriksen P.: Effective yttrium based coating for steel interconnects of solid oxide cells: Corrosion evaluation in steam-hydrogen atmosphere// JOURNAL OF POWER SOURCES -Vol. 440, (2019), s.226814-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jpowsour.2019.226814
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 164 razy
Publikacje, które mogą cię zainteresować
Low temperature processed MnCo2O4 and MnCo1.8Fe0.2O4 as effective protective coatings for solid oxide fuel cell interconnects at 750 °C
- S. Molin,
- P. Jasiński,
- L. Mikkelsen
- + 3 autorów
Ceria Based Protective Coatings for Steel Interconnects Prepared by Spray Pyrolysis
- D. Grudzień,
- M. Chen,
- S. Molin
- + 2 autorów