Environmental degradation of titanium alloy in artificial saliva

Andrzej Zieliński; Łukasz Zborowski - Weychman

doi:10.2478/v10077-012-0008-1

Environmental degradation of titanium alloy in artificial saliva

Abstrakt

The titanium and its alloys are potentially prone to hydrogen embrittlement, including those proposed for dental implants. The research has been aimed to assess a susceptibility to environment-enhanced degradation of the Ti-13Zr-13Nb alloy in artificial saliva with or without hydrofluoric acid, subject or not to cathodic polarisation. The results have shown that even if artificial saliva is safe environment, both cathodic polarization and cathodic current result in brittle cracking. Either hydride-related embrittlement or fluoride-related stress corrosion cracking are considered as potential sources.

Cytowania

0

CrossRef
0

Web of Science
0

Scopus

Autorzy (2)

Cytuj jako

Pełna treść

pobierz publikację

pobrano 5 razy

Wersja publikacji: Accepted albo Published Version
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/v10077-012-0008-1
Licencja: otwiera się w nowej karcie

Słowa kluczowe

Informacje szczegółowe

Kategoria:: Publikacja w czasopiśmie
Typ:: artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
Opublikowano w:: Advances in Materials Science nr 12, wydanie 3, strony 5 - 15,
ISSN: 1730-2439
Język:: angielski
Rok wydania:: 2012
Opis bibliograficzny:: Zieliński A., Zborowski - Weychman Ł.: Environmental degradation of titanium alloy in artificial saliva// Advances in Materials Science. -Vol. 12., iss. 3 (2012), s.5-15
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/v10077-012-0008-1
Weryfikacja:: Politechnika Gdańska