Fabrication, Microstructure and High Temperature Corrosion Resistance of Porous Alloys for Solid Oxide Fuel Cells
Abstrakt
Porous alloys find use in modern Solid Oxide Fuel Cells as the supporting structures. As they are exposed to high temperatures (> 500°C) an oxide scale forms on their surface due to high temperature corrosion phenomena. Since the ratio between the surface area and volume is much higher than for planar samples, formation of the oxide can lead to a breakaway oxidation after relatively short times. Therefore corrosion properties of possible candidate alloys should be studied. In this work corrosion kinetics of IN625 alloy is studied in the temperature range of 700°C – 800°C in air and hydrogen atmosphere for up to 100 hours. Moreover, a method of reducing corrosion rates of porous alloys by the infiltration of simple rare earths elements is shown. Modification by the Y precursor reduces corrosion rate by a factor of 50 in air at 700°C so that the lifetime of the infiltrated alloy is greatly extended.
Autorzy (5)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Aktywność konferencyjna
- Typ:
- publikacja w wydawnictwie zbiorowym recenzowanym (także w materiałach konferencyjnych)
- Tytuł wydania:
- 5th International Conference FDFC 2013 : Fundamentals &Development of Fuel Cells strony 1 - 9
- Język:
- angielski
- Rok wydania:
- 2013
- Opis bibliograficzny:
- Molin S., Dunst K., Biczyńska M., Karczewski J., Jasiński P.: Fabrication, Microstructure and High Temperature Corrosion Resistance of Porous Alloys for Solid Oxide Fuel Cells// 5th International Conference FDFC 2013 : Fundamentals &Development of Fuel Cells/ Karlsruhe: , 2013, s.1-9
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 138 razy
Publikacje, które mogą cię zainteresować
THE ROLE OF THIN FUNCTIONAL LAYERS IN SOLID OXIDE FUEL CELLS
- S. Molin,
- A. Chrzan,
- J. Karczewski
- + 2 autorów