Abstrakt
To further understand the suitability of Ni-Cr-base alloy for solid oxide fuel cell (SOFC), a commercial Ni-Cr-Fe-Mo alloy, Hastelloy X was selected and evaluated for oxidation behaviour under high temperature conditions. HastelloyX was chosen due to its unusual resistance to oxidizing, reducing and neutral atmospheres. For long term stability of metal supported fuel cell, the corrosion resistance plays a vital role and must be enhanced. Cyclic thermogravimetric analysis, X-ray diffractometry and SEM imaging were used to describe properties of these porous alloy. The influence of porosity on resulting properties was also elucidated. The high temperature corrosion rate is high and is strongly influenced by the porosity level. Open porosity decreases rapidly upon oxidation at 800 ºC.
Autorzy (5)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Zeszyty Naukowe Wydziału ETI Politechniki Gdańskiej. Technologie Informacyjne
strony 17 - 23,
ISSN: 1732-1166 - Język:
- angielski
- Rok wydania:
- 2012
- Opis bibliograficzny:
- Dunst K., Biczyńska M., Karczewski J., Jasiński P., Molin S.: High temperature corrosion resistance of porous hastelloy alloy// Zeszyty Naukowe Wydziału ETI Politechniki Gdańskiej. Technologie Informacyjne. -., nr. 20 (2012), s.17-23
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 149 razy
Publikacje, które mogą cię zainteresować
THE ROLE OF THIN FUNCTIONAL LAYERS IN SOLID OXIDE FUEL CELLS
- S. Molin,
- A. Chrzan,
- J. Karczewski
- + 2 autorów