Fully bio-based poly(propylene succinate) synthesis and investigation of thermal degradation kinetics with released gases analysis
Abstrakt
One of the most important information about polyesters is their thermal stability and phase transition tem- peratures. These characteristics give information about the promising behavior of the polyester during proces- sing. In this work, linear bio-based polyester polyols were prepared with the use of succinic acid and 1.3- propanediol (both with natural origin). As a polycondensation catalyst was used tetraisopropyl orthotitanate (TPT), which different amount was employed. The thermogravimetric analysis allowed to observe high thermal stability and one step of the thermal decomposition. This analysis affirmed also that the catalyst content did not influence the thermal degradation characteristics of the prepared polyols. Nevertheless, it has huge importance in the context of thermal degradation kinetics. It was determined with the use of Ozawa, Flynn, and Wall and Kissinger's methods to verifying catalyst impact on the thermal degradation kinetics. Moreover, probable me- chanism of the prepared bio-based polyols thermal degradation was proposed based on the QMS results.
Cytowania
-
2 3
CrossRef
-
0
Web of Science
-
2 9
Scopus
Autorzy (3)
-
Iwona Koltsov dr inż.
- Polska Akademia Nauk Instytut Wysokich Ciśnień
-
Janusz Datta prof. dr hab. inż.
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
POLYMER DEGRADATION AND STABILITY
nr 151,
strony 90 - 99,
ISSN: 0141-3910 - Język:
- angielski
- Rok wydania:
- 2018
- Opis bibliograficzny:
- Parcheta P., Koltsov I., Datta J.: Fully bio-based poly(propylene succinate) synthesis and investigation of thermal degradation kinetics with released gases analysis// POLYMER DEGRADATION AND STABILITY. -Vol. 151, (2018), s.90-99
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.polymdegradstab.2018.03.002
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 188 razy