Abstrakt
The new poly(ester-ether urethane)s (PEEUR) were prepared in two stage synthesis from formerly obtained oligo(alkylene ester-ether)diols (OAEE) and 4,4‘-diphenylmethane diisocyanate (MDI). PEEUR samples were subjected to crosslinking with styrene in the presence of radical polymerization initiators: methyl ethyl ketone peroxide (MEKPO) or cobalt 2-ethyl cyclohexanoate (EtHCo). Crosslinked PEEUR were characterized by their physicochemical and mechanical properties. Tensile strength of crosslinked PEEURs was in the range 63-29 MPa, hardness values were from 92 to 97°ShA, and glass transition temperature was in the range 59-74°C. For PEEURs filled with biocides tensile strength was in the range 6,8-8,5MPa, hardness values were from 82 to 92°ShA, and glass transition temperature was in the range 57-72°C. Optical microscopic observations showed that the materials obtained were homogeneous in micrometric scale.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/adms-2013-0001
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Advances in Materials Science
nr 13,
strony 5 - 10,
ISSN: 1730-2439 - Język:
- angielski
- Rok wydania:
- 2013
- Opis bibliograficzny:
- Kucińska-Lipka J., Janik H., Gubańska I.: Novel Polyurethanes as Antifouling Paint Matrices// Advances in Materials Science. -Vol. 13., nr. 1 (2013), s.5-10
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/adms-2013-0001
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 111 razy
Publikacje, które mogą cię zainteresować
Synthesis and characterisation of polyurethane elastomers with semi-products obtained from polyurethane recycling
- P. Jutrzenka Trzebiatowska,
- T. Calvo-Correas,
- A. Eceiza
- + 1 autorów
The changes of crosslink density of polyurethanes synthesised with using recycled component. Chemical structure and mechanical properties investigations.
- P. Jutrzenka Trzebiatowska,
- A. Santamaria-Echart,
- T. Calvo-Correas
- + 2 autorów