Physicochemical properties of Mn1.45Co1.45Cu0.1O4 spinel coating deposited on the Crofer 22 H ferritic steel and exposed to high-temperature oxidation under thermal cycling conditions
Abstrakt
The Crofer 22 H ferritic steel substrate was coated with an Mn1.45Co1.45Cu0.1O4 spinel by means of electrophoresis. After high-temperature oxidation under thermal cycling conditions, the physicochemical properties of the obtained system were evaluated. During 48-h cycles that involved heating the samples up to temperatures of either 750 or 800 °C, the oxidation kinetics of both coated and unmodified steel approximately obeyed the parabolic rate law. The unmodified steel was oxidized at a higher rate than the system consisting of the substrate and the coating. In its bulk form, the spinel consisted entirely of the cubic phase and it exhibited high electrical conductivity. The Mn1.45Co1.45Cu0.1O4 coating, on the other hand, was compact and consisted of two phases—the cubic and the tetragonal one—and it was characterized by good adhesion to the metallic substrate. After cyclic oxidation studies conducted for the two investigated temperatures (750 or 800 °C), the coat- ing was determined to provide a considerable improvement in the electrical properties of the Crofer 22 H ferritic steel, as demonstrated by the area-specific resistance values measured for the steel/coating system. The evaporation rate of chromium measured for these samples likewise indicates that the coating is capable of acting as an effective barrier against the formation of volatile compounds of chromium. The Mn1.45Co1.45Cu0.1O4 spinel can therefore be considered a suitable material for a coating on the Crofer 22 H ferritic steel, with intermediate-temperature solid oxide electrolyzer cells as the target application.
Cytowania
-
8
CrossRef
-
0
Web of Science
-
1 3
Scopus
Autorzy (6)
-
Łukasz Mazur
- AGH University of Science and Technology
-
Jarosław Dąbek
- AGH University of Science and Technology
-
Karol Durczak
- Poznan University of Life Sciences
-
Michał Pyzalski
- AGH University of Science and Technology
-
Tomasz Brylewski
- AGH University of Science and Technology
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/s10973-021-10884-2
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY
nr 147,
strony 5649 - 5666,
ISSN: 1388-6150 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Mazur Ł., Molin S., Dąbek J., Durczak K., Pyzalski M., Brylewski T.: Physicochemical properties of Mn1.45Co1.45Cu0.1O4 spinel coating deposited on the Crofer 22 H ferritic steel and exposed to high-temperature oxidation under thermal cycling conditions// JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY -Vol. 147, (2022), s.5649-5666
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/s10973-021-10884-2
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 126 razy
Publikacje, które mogą cię zainteresować
Influence of Gd deposition on the oxidation behavior and electrical properties of a layered system consisting of Crofer 22 APU and MnCo2O4 spinel
- T. Brylewski,
- S. Molin,
- M. Marczyński
- + 4 autorów
Multilayer coatings based on cerium oxide and manganese cobaltite spinel for Crofer22APU SOC interconnects
- E. Zanchi,
- J. Ignaczak,
- G. Cempura
- + 3 autorów