Pre-oxidation of porous ferritic Fe22Cr alloys was extensively studied in this paper. Weight gain measurements and SEM analysis revealed that pre-oxidation performed at 900◦C for 40 min increased the lifespan of the alloy. A Cr evaporation study did not disclose any significant influence of the pre-oxidation process on the Cr content in the alloy. For a more detailed assessment, TEM imaging and X-ray tomography measurements of pre-oxidized samples were performed. These analyses showed that alteration in the grain and grain boundary diffusion fluxes might be the key for explaining the corrosion prevention role of pre-oxidation.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (7)
-
Małgorzata Makowska Dr.
-
F. Marone
-
Grzegorz Cempura dr inż.
-
Matthieu Tomas
-
Jan Froitzheim
Cytuj jako
Pełna treść
pobierz publikację
pobrano 60 razy
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.corsci.2024.112129
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
CORROSION SCIENCE
nr 234,
strony 112 - 129,
ISSN: 0010-938X - Język:
- angielski
- Rok wydania:
- 2024
- Opis bibliograficzny:
- Koszelow D., Makowska M., Marone F., Cempura G., Tomas M., Froitzheim J., Molin S.: Pre-oxidation of porous ferritic Fe22Cr alloys for lifespan extension at high-temperature// CORROSION SCIENCE -,iss. 234 (2024), s.112-129
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.corsci.2024.112129
- Źródła finansowania:
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 46 razy