Polycrystalline samples of HoT2Al20 (T = Ti, V, Cr) intermetallics were synthesized using a step-wise arc-melting technique. All three compounds adopt the CeCr2Al20-type crystal structure with Ho atoms positioned inside oversized icosahedral cages formed by Al atoms. The structure of HoV2Al20 compound is reported. The materials properties were studied by means of electrical resistivity, magnetic susceptibility, and specific heat measurements. All three compounds show a Curie-Weiss paramagnetic behavior down to 1.95 K. Specific heat measurements show the presence of electronic Schottky anomaly resulting from crystal-field splitting of Ho3+ energy levels in the three compounds, while in HoTi2Al20 and HoV2Al20 a second anomaly was observed, resulting from the presence of low-energy Einstein phonon mode.
Cytowania
-
1 5
CrossRef
-
0
Web of Science
-
1 5
Scopus
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
INTERMETALLICS
nr 85,
strony 103 - 109,
ISSN: 0966-9795 - Język:
- angielski
- Rok wydania:
- 2017
- Opis bibliograficzny:
- Winiarski M., Klimczuk T.: Synthesis and properties of HoT2Al20 (T = Ti, V, Cr) intermetallic cage compounds// INTERMETALLICS. -Vol. 85, (2017), s.103-109
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.intermet.2017.02.005
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 163 razy
Publikacje, które mogą cię zainteresować
Synthesis and properties of AxV2Al20 (A = Th, U, Np, Pu) ternary actinide aluminides
- M. J. Winiarski,
- J. Griveau,
- E. Colineau
- + 5 autorów