Synthesis of CoFe2O4 Nanoparticles: The Effect of Ionic Strength, Concentration, and Precursor Type on Morphology and Magnetic Properties
Abstrakt
The present study highlights the effect of metal precursor types (SO4 2¯, Cl¯, and NO3¯), their concentration, and the influence of ionic strength of reaction environment on the morphology, surface, and magnetic properties of CoFe2O4 particles. The magnetic nanoparticles were obtained by chemical coprecipitation in alkaline medium at increasing metal concentration in the range of 0.0425 mol·dm-3 to 0.17 mol·dm-3 and calcination temperature from 400°C to 800°C. It was found that the chemistry of precursors can be directly correlated with magnetic properties. The CoFe2O4 particles from metal sulphate precursors showed the highest saturation magnetization and the lowest coercivity. The adjustment of ionic strength in the range of 1.25–5M was achieved by adding an appropriate quantity of metal sulphates into aqueous solutions at a constant pH or by adding an appropriate quantity of NaClO5 under similar conditions. The average hydrodynamic size of CoFe2O4 increased from 46nm to 54 nm with increasing metal concentration and ionic strength. An explanation of magnetic properties, caused by ionic strength and metal concentration, is given based mainly on the reduction in repulsive forces at the particle interface and compensation of the double electric layer in the presence of anions. The observed coercivity was lower for the particles obtained in solutions with the highest ionic strength, whereas the concentration of metals and calcination temperature affected the saturation magnetization and morphology of the obtained cobalt ferrite particles.
Cytowania
-
3 0
CrossRef
-
0
Web of Science
-
3 3
Scopus
Autorzy (5)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Journal of Nanomaterials
nr 2020,
strony 1 - 12,
ISSN: 1687-4110 - Język:
- angielski
- Rok wydania:
- 2020
- Opis bibliograficzny:
- Malinowska I., Ryżyńska Z., Mrotek E., Klimczuk T., Zielińska-Jurek A.: Synthesis of CoFe2O4 Nanoparticles: The Effect of Ionic Strength, Concentration, and Precursor Type on Morphology and Magnetic Properties// Journal of Nanomaterials -Vol. 2020, (2020), s.1-12
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1155/2020/9046219
- Źródła finansowania:
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 199 razy
Publikacje, które mogą cię zainteresować
Magnetic photocatalysts for water treatment
- A. Zielińska-Jurek,
- S. Dudziak,
- Z. Bielan
- + 3 autorów
Electrochemical cobalt oxidation in chloride media
- I. Makarava,
- J. Vanska,
- A. Kramek
- + 4 autorów
Dielectric Spectroscopy Studies and Modelling of Piezoelectric Properties of Multiferroic Ceramics
- A. Lisińska-Czekaj,
- D. Czekaj,
- B. Garbarz-Glos
- + 3 autorów