Timber is traditionally dried in kilns by processes that often take several days or weeks to complete. At present, it is possible to apply several methods of rapid drying of timber, including, for example, press drying. This research is based on the use of this process. Drying was performed using the heating plates with a temperature of 160 °C. Three pressures were compared in the research 1.0 MPa, 1.4 MPa, and 1.8 MPa. The density...

The technology of high temperature drying has a great inuence on dimensional and selected physical changes in tension wood. Article is focused on the measurement properties such as moisture content, color changes and longitudinal warping. The quality of beech wood is determined based on structure and properties of wood, frequency of defects in wood material. The tension wood is considered as an important wood defect causing negative...

The modern wood converting processes consists of several stages and material drying belongs to the most influencing future performances of products. The procedure of drying wood is usually realized between subsequent sawing operations, affecting significantly cutting conditions and general properties of material. An alternative methodology for determination of mechanical properties (fracture toughness and shear yield stress) based...

The aim of the article is to present the influence of high temperature to selected properties of beech wood (Fagus sylvatica L.). The properties such as moisture content, color changes and longitudinal warping were analyzed. The quality of beech wood is determined based on structure and properties of wood, frequency of defects in wood material. The tension wood is considered as an important wood defect causing negative alterations...

The results of experimental research on the colour changes of beech wood at different depths of the tested layer are presented. Beech wood (Fagus sylvatica L.) dried in a conventional kiln was tested. Half of the wood samples were steamed prior to the drying process. Colour changes were measured at various depths after the face milling process was used to remove the material to expose to the deeper surface. The colour changes were...