This paper presents the hydrogen reduction behaviour of industrial pellets designed for the efficient hydrogen based direct reduction. The pellets were provided with very low non ferrous oxides percentage (0.52 of basicity index) and with the absence on TiO2 oxides. The pellets measured diameters in the range 1.14–1.72 cm and were characterized in terms of porosity, pores size, tortuosity and compression strength. The pellets were...

High grade pellets with basicity index close to 0.5 were directly reduced in pure hydrogen atmosphere. The reduction experiments were performed in the temperature range 800 e1000 C at the pressure of 8 bar. The pellets internal structure was analysed through micro tomography observations in the unreduced and reduced conditions. After reduction, the pellets showed a variation of porosity up to more than 15% with a remarkable change...

A reduction of bismuth oxide in hydrogen atmosphere was investigated. The reaction was performed with a material in various structural forms: powder: with micrometric grains, powder with nanometric grains and powder pressed into pellets. The process was performed in both isothermal and non-isothermal conditions. An activation energy of the reaction calculated with Friedman method was found to be about 85 kJ/mol for the reduction...

Reduction in a hydrogen atmosphere of Bi2O3, Sb2O3 and TeO2 mixes oxides for the synthesis of BiSbTe3 was analysed. The reduction reactions of Sb2O3 and Sb2O4 oxides, as well as Bi2O3+Sb2O3 and Sb2O3+3TeO2 mix- tures, were also evaluated. The reduction of Sb2O4 is investigated for the first time. The reactions of the mixed oxides systems also were not the subject of research so far despite being used for synthesis of the (Bi,Sb)2Te3...