The paper describes structure and properties of dissimilar stainless steels welded joints between duplex 2205 and austenitic 316L steels. Investigations were focused on environmentally assisted cracking of welded joints. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement was determined in slow strain rate tests (SSRT) with the strain rate of 2.2 × 10–6 s–1. Chloride-inducted SCC was determined in the...

Stress corrosion cracking resistance of cold worked layers of 25 Cr duplex stainless steel grade UR52N+ has been investigated. The surface layers were performed through burnishing treatment. The residual stresses at surface layers were determined using grazing angle incidence X-ray diffraction method (g-sin2 Ψ). Corrosion tests were performed with the use of Slow Strain Rate Test technique in boiling 35% MgCl2 solution. It has...

The paper presents the results of a laboratory investigation of the microbiologically assisted hydrogen‐induced stress cracking (HISC) of 2,205 duplex stainless steel (DSS). The testing of susceptibility toward HISC was performed with two different methods. Precharged in sulfate‐reducing bacteria (SRB), inoculated medium samples were subjected to slow strain‐rate testing in artificial seawater. In situ constant load tests were...

The effect of cathodic polarization conditions on hydrogen degradation of X2CrNiMoCuN25-6-3 super duplex stainless steel welded joints, obtained using flux cored arc and submerged arc welding methods, was evaluated. Slow strain rate tensile tests of base material and welded specimens, ferrite content measurements, scanning electron microscopy observations, and statistical analysis were performed. It was found that hydrogenation...

The present research was aimed at determining the effects of the oxide layers on hydrogen absorption, microstructure and mechanical properties of the Zircaloy- 2 and Zr 702 alloys. The oxidation was made at 350 °C, 700 °C and 900 °C for 10 to 30 min in laboratory air, followed by hydrogen cathodic charging for 72 h and annealing at 400 °C for 4 h. The slow strain rate tests were carried out on oxidized, charged and annealed specimens. The...