Rok 2024
-
The effect of preliminary creep-strain on material behavior under LCF tension/compression and pure torsion regimes
PublikacjaThis paper presents the results of experimental tests of monotonic tension and torsion, creep-rupture and preliminary creep at 200C and 300C, as well as low-cycle fatigue of 2024 T3511 aluminum alloy. The fatigue process was conducted at room temperature for uniaxial tension/compression and torsion. The as-received material and pre-deformed material were also investigated during creep at elevated temperature. Basic monotonic,...
Rok 2023
-
Experimental ultimate strength assessment of stiffened plates subjected to marine immersed corrosion
PublikacjaThis study experimentally analyses the impact of marine immersed corrosion degradation on the compressive strength of the stiffened plates where the lower degradation levels were considered. The corrosion degradation test was accelerated by controlling the natural corrosion environmental factors, avoiding applying an electric current. Different groups of corrosion degradation levels and initial plate thicknesses were investigated....
-
Fractographical quantitative analysis of EN-AW 2024 aluminum alloy after creep pre-strain and LCF loading
PublikacjaThis paper explores the applicability of a new damage parameter combining both fracture surface topography and loading features to estimate the fatigue lifetime under creep pre-strain and low-cycle fatigue loading. Fractures of EN-AW 2024 aluminum alloy caused by mixed creep and low-cycle fatigue loading are experimentally characterized and quantified via surface topography analysis. The specimens were preliminary damaged in a...
-
Latent fingerprint imaging by spectroscopic optical coherence tomography
PublikacjaOptical coherence tomography (OCT) is a non-contact and non-invasive optical method for evaluating semitransparent and scattering objects. Its unique features, such as non-destructive 3D measurements of tested objects with a fast scanning rate, make this technique interesting for latent fingerprint reading, which is the subject of this paper. So far, OCT has not found widespread use for reading fingerprints directly from surfaces...
-
Multi-functional monodispersed SiO2-TiO2 core-shell nanostructure and TEOS in the consolidation of archaeological lime mortars surfaces
PublikacjaArchaeological traditional lime mortars are susceptible to many environmental conditions such as the impact of water (rain, humidity, groundwater, etc.), variation of temperatures' degrees, wind and/or pollution. Accordingly, this research aims to provide newly assessed multifunctional Nano-coating for the purpose of archaeological lime mortar protection. For this, the study combined physicochemical and mechanical characterizations...
-
ROLE OF GREEN LOGISTICS IN THE CONSTRUCTION OF SUSTAINABLE SUPPLY CHAINS
PublikacjaThe global supply chain has been growing strongly in recent years. This development brings many benefits to the economy, society, and human resources in each country but also causes a large number of concerns related to the environment since traditional logistics activities in the supply chain have been releasing significant amount of emissions. For that reason, many solutions have been proposed to deal with these environmental...
-
The elasto-plastic numerical study of crack initiation in notched PMMA specimens under uniaxial loading conditions – Tension and torsion
PublikacjaThis paper presents the results of FEM numerical calculations aimed at describing the plastic strain and stress fields under critical loading conditions: tensile force or torsional moment. The calculations were carried out with reference to the results of experimental tensile and torsional tests of flat PMMA specimens weakened with V-notches of different root radii: 0.5, 2 and 10 mm. The procedure for conducting nonlinear numerical...
-
The fracture behaviour of notched PMMA specimens under simple loading conditions – Tension and torsion experimental tests
PublikacjaThis paper presents the results of experimental testing of flat PMMA specimens during uniaxial loading conditions. Two separate tests were conducted: tensile and torsion. The specimens were weakened with V-type edge notches with different root radii: 0.5; 2 and 10 mm. The specimens were made in two thickness variants: 5 and 15 mm. Monotonic tensile and torsion tests were carried out while keeping the averaged strain rate constant,...
Rok 2022
-
Crack Mouth Opening Displacement for EH36 Shipbuilding Steel Measurements
PublikacjaThe dataset titled EH36 steel for shipbuilding (plate thicnkness 50mm) - CMOD - force record, a0/W = 0.6 contains CMOD (Crack Mouth Opening Displacement) - Force record which is the base for evaluation of fracture toughness of structural steel. Bend specimens witch Bx2B section (B= 50mm), and relative initial crack length a0 / W = 0.60 were used. The test was carried out at ambient temperature in accordance to ISO 12135 standard....
-
Experimental investigations and damage growth modeling of EN‐AW 2024 aluminum alloy under LCF loading accounting creep pre‐deformation
PublikacjaThis article presents the results of experimental tests of creep rupture and of low-cycle fatigue (LCF) of EN-AW 2024 aluminum alloy devoid of damage and having preliminary damage. The preliminary damage was dealt in the process of creep at elevated temperature 100C, 200C, and 300C until achievement of two different strain values at each temperature. Samples with preliminary damage were subjected to fatigue tests at room temperature....
-
Fatigue of titanium alloy Ti6Al4V with diamond structure obtained by Laser Power Bed Fusion method
PublikacjaThis paper presents the results of fatigue tests conducted on Ti6Al4V titanium alloy with diamond structure obtained by the Laser Power Bed Fusion method. Samples used in tests were printed with porosities: 81%, 73%, 50%, 34% and near-zero porosity. Samples were subjected to cyclic tests with a constant stress amplitude. The number of cycles until sample failure was registered. Obtained fatigue test results made it possible to...
-
Influence of Material Thickness on the Ductile Fracture of Steel Plates for Shipbuilding
PublikacjaIn the shipbuilding industry, the risk of brittle fractures is relatively high because some units operate in arctic or subarcticzones and use high thickness (up to 100 mm) steel plates in their structures. This risk is limited by employing certifiedmaterials with a specific impact strength, determined using the Charpy method (for a given design temperature) and byexercising control over the welding processes (technology qualification,...
-
Prediction of Weld Deformations by Numerical Methods - Review
PublikacjaThe welding process is the basic technique of joining in the shipbuilding industry. This method generates welding distortions that cause a lot of problems during the manufacturing process due to both the time and cost of straightening as well as their influence on later stages of production. Proper preparation of welding processes plays a growing role in the shipbuilding industry and the development of calculating tools is being...
Rok 2021
-
EXPERIMENTAL AND NUMERICAL INVESTIGATION ON SPECIMEN GEOMETRY EFFECT ON THE CTOD VALUE FOR VL-E36 SHIPBUILDING STEEL
PublikacjaThere are special cases in the marine industry, where additional material tests, such as the fracture toughness test, must be performed. Additional fracture toughness tests, such as CTOD (Crack Tip Opening Displacement), are typically performed on three-point bend specimens. The dimension that defines all the specimen dimensions is the thickness of the material to be tested. It is recommended by classification societies (e.g. DNVGL)...
-
Indoor accelerated controlled corrosion degradation test of small- and large-scale specimens
PublikacjaThe work presented here is a part of a long-term project analysing the structural behaviour of ageing marine structures. An accelerated corrosion degradation set-up was developed to reproduce corroded marine structural specimens of different degrees of degradation, controlling various natural factors, i.e., temperature, oxygen content, salinity, and flow velocity. The nine stiffened plates of 1.2 m length and 30 small scale specimens...