This paper concerns an inspection of a water supply system, made of AISI 304 steel, which showed signs of local corrosion at the weld. Such corrosion caused material perforation after very short periods of operation. It was revealed that steel was sensitised during the welding process. It was also proven that chromium micro-segregation occurred in the alloy leading to galvanic cell formation which initialised the process of pitting corrosion. This paper is a study of corrosion attack types due to negligence during and after the process of welding of the system.
Cytowania
-
9
CrossRef
-
0
Web of Science
-
6
Scopus
Autorzy (3)
Cytuj jako
Pełna treść
pobierz publikację
pobrano 21 razy
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.conbuildmat.2014.04.058
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
CONSTRUCTION AND BUILDING MATERIALS
nr 64,
strony 246 - 252,
ISSN: 0950-0618 - Język:
- angielski
- Rok wydania:
- 2014
- Opis bibliograficzny:
- Ryl J., Wysocka J., Darowicki K.: Determination of causes of accelerated local corrosion of austenitic steels in water supply systems// CONSTRUCTION AND BUILDING MATERIALS. -Vol. 64, (2014), s.246-252
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.conbuildmat.2014.04.058
- Weryfikacja:
- Politechnika Gdańska
Powiązane datasety
wyświetlono 126 razy
Publikacje, które mogą cię zainteresować
Effects of preheating on laser beam–welded NSSC 2120 lean duplex steel
- M. Landowski,
- S. C. Simon,
- C. Breznay
- + 2 autorów
2024